热作模具钢H13Nb锻造模块组织和性能研究
马野，刘宝石，燕云，刘明
抚顺特殊钢股份有限公司技术中心（辽宁抚顺113001)
【摘要】对H13加入微量合金元素Nb热作模具钢锻造模块的显微组织和机械性能进行了研究，结果表明：采用EAF+LF+VD+ESR工艺可以生产出高纯净度的H13Nb钢。不率回火处理及率回火处理后的H13Nb钢都拥有优良的横向冲击及拉伸性能，同时显微组织均匀，
与相同工艺生产的H13钢相比较冲击韧性有所提高，显微组织差别不大。关键词：锻造模块；显微组织；机械性能；冲击
中图分类号：TG659；TG142.45
文献标识码：B
Study on Microstructure and Properties of Hi3NbHotWorkDieForgingModule
[Abstract] In this paper the H13 adding alloy elements of Nb hot forging microstructure and mechanical properties of die steel were studied. The results showed that the EAF+LF+VD+ESR process can produce high-purity steel H13Nb. No quenching tempering treatment and quenching tempering of H13Nb steel with transverse impact and excellent tensile properties. At the same time homogeneous microstructure, compared with the same H13 steel production process impact toughness increased, little difference in microstructure.
Key words :forging module; microstructure; mechanical properties; impact
1引言
热作模具钢主要用于制造对高温状态的金属进行热成形的模具，如热锻模具、热挤压模具、压铸模
其中，芯轴最下端为外螺纹，紫色的部分表示其受力在2.931x10-~29.26MPa，紫色和浅黄色都有的部分受力最复杂，也是最危险的部位，受力在2.931x 10-3~233.9MPa，紫色和蓝色的部分受力也在2.931× 10-~58.49MPa，均低于其屈服应力355MPa，故该芯轴
满足强度要求，可以安全的使用。 4结束语
实践证明，文中所介绍的壳体模具型芯零件的车床夹具，操作方便，定位准确，结构紧凑且简单，加工效果较好，它为解决此套类模具零件的装夹加工提供借鉴，具有一定的参考意义。
参考文献
《模具制造》2017年第6期方方数据
具、热剪切模具等。H13是一种典型的热作模具钢，具有优良的热强性、塑韧性、抗氧化性及热疲劳抗力，一般在400℃~600℃热作场合下服役，适合制造各类
[川]南文虎，肖根先，王宏，一种自动定心夹具的设计]]机床
与液压,2011,39(18)：32~33
[2]李银玉，吴敬，定位套零件钻孔加工夹具设计J]机床与液
压,2016,44(16),75~76
[3]王先遂.机械加工工艺规程制定[M]北京：机械工业出版
社，2008.
[4]陈文．一种不停车胀胎车夹具的设计与应用[]机床与液
压,2015,43(20):178~182
[5】孙丽媛.机械制造工艺及专用夹具设计指导[M].北京：冶金
T业出版社，2010.
作者简介：李学兵，男，1979年生，湖北黄冈人，讲师，东北大学研究生学历，硕士学位，现任辽宁轨道交通职业学院数控工程系数控教研室教师，主要从事
机械及数控教学和加工。
（收稿日期：2017-01-16）cwm
. 77 ·