ISSN10003762 CN41 1148/TH
轴承2016年12期 Bearing 2016 , No. 12
轴承与轴材料热膨胀系数不匹配导致的磨损
问题分析
孙东，赵燕，张静静，李正辉，林大鹏（中航工业哈尔滨轴承有限公司，哈尔滨150000）
31 33
摘要：针对主机主轴承与配合轴异常磨损故障，对轴承和轴的材料进行分析，结果证明，轴承内径面及轴异常磨
损与材料热膨胀系数不匹配有关，并对此提出改进措施，经验证，改进后轴承磨损问题得到解决。关键词：滚动轴承；热膨胀系数；异常磨损
中图分类号：TH133.33；0343.3
文献标志码：B
文章编号：10003762(2016)12003103
Analysis onWearCausedbyUnmatchedThermalExpansionCoefficient
of Bearing and Shaft Material
Sun Dong, Zhao Yan, Zhang Jingjing, Li Zhenghui, Lin Dapeng
( AVIC Harbin Bearing Co. , Ltd. , Harbin 150000, China)
Abstract: Aiming at abnormal wear fault for main bearing and shaft of main egine, the material of bearing and shaft is analyzed. The results show that the abnormal wear of inner rings of bearings and shaft are related to unmatched thermal expansion coefficient of material, and the improvement measures are put forward. It is proven that the wear problem is solved afier improvement.
Key words : rolling bearing; coefficient of thermal expansion; abnormal wear
轴承与轴之间以过盈配合为主，可有效防止
内圈与轴之闻的相对滑动，避免非正常的磨损。收稿日期：2016-04-07；修回日期：2016-0621
作者简介：孙东（1985一），男，工程师，主要从事基础研究工作,E mail: zebral897@163. com
轴承与轴配合时需对载荷类型、载荷大小、零件结构等因素进行考虑，以确保轴承的正常使用，
普通工况下，轴承工作温度不高于120℃，选取轴承时，材料热膨胀系数的匹配性不会对使用性能产生影响，故往往予以忽略。而在航空主机、
续表
缺陷类型夹杂
3
混合料内存在杂质模具清理不干净工作环境不清洁
结束语
产生原因
总结了复合材料制造过程中易出现缺陷的具
体表现，分析了产生缺陷的原因，并逐一给出了解决方案，有助于本领域相关人员快速参照采取改进措施，降低复合材料的废品率。
万方数据
参考文献：
解决方案
改善混料环境质量，避免在混料工序引人杂质认真清理模腔，保证腔体洁净
生产环境应符合要求，人员工作服应整洁
[]
孙小波，王子君，王枫.轴承保持架用聚酰亚胺材料[J].轴承,2013(9);5457.
[2]
李国能，张治国塑料模压成形技术问答［M]．北京：印刷工业出版社，2012.
（编辑：王玉良）