机械制造文摘—焊接分册
高Cr奥氏体型不锈钢气体
保护焊用焊接材料刘策”，马树忠"，艾梓涵”，何少卿”
（1.锦州万得焊材有限公司，辽宁锦州121213：
2.宏启胜精密电子（秦皇岛）有限公司，河北秦皇岛066004；
3.锦州市特种设备监督检验所，辽宁锦州121000）
了研究。
关键词：高Cr奥氏体型不锈钢：焊接材料：工艺性能中图分类号：TC422
AkindofhighCrausteniticstainlesssteelwelding
material used in gas shielded welding Liu Ce',Ma Shuzhong', Ai Zihan’, He Shaoqing
(1. Jinzhou Wonder Welding Material Co. , LTD, Jinzhou 121213, Liaoning, China; 2. Hongqisheng Precision Electronic Co., LTD, Qinhuangdao 066004, Hebei, China ;
专利信息
3. Jinzhou Special Equipment Supervision and Inspection Institute, Jinzhou 121000, Liaoning, China)
Abstract: The high temperature and pressure environment for thermal power plants at home and abroad require new types of welding materials. A kind of high Cr austenitic stainless steel welding material was developed in this research, and it process performance were studied.
Key words: high Cr austenitic stainless steel; welding material; process performance
概述 1
近年来，在国内外的火力发电厂中，由于蒸汽条件的高温高压化，要求使用螨变强度比18Cr-8Ni型不锈钢高的耐热钢，因此开发了20-25Cr型奥氏体不锈钢。对于焊接材料，开发了改善高温特性的19Cr-11.5Ni-0.1C型不锈钢焊接用焊丝和焊条。但是对于更高要求的高温高压环境的焊接材料尚未开发，为了满足20-25Cr型奥氏体不锈钢的焊接，研究了高Cr奥氏体型不锈钢，特别是20-25Cr型焊接材料的优良蜗
万方数据
变特性，研发了高温高压环境下具有更高要求的高Cr 奥氏体型不锈钢焊接材料。
发明的内容 2
2.1气体保护焊用焊丝的合金含量及其作用
C:0.02%~0.1%，C是降低耐腐蚀性的成分。超过0.1%时，产生晶间腐蚀。小于0.02%时，降低蠕变强度。因此，C含量控制在0.02%~0.1%范围内。
Si:0.1%~1.0%，Si是脱氧剂，是改善熔融金属流
17
2016年第2期