配合煤中添加硼系化合物对焦炭性质的影响
严铁军王光辉舒大凡石晓明赵磊周施（武汉科技大学化学工程与技术学院，武汉430081）
5
摘要：考察了不同硼系化合物及添加量对配合煤和焦炭性质的影响。BO、BA、BX加入配合煤中均会使配合煤黏结性和焦炭冷强度劣化，并且随着加人量的增加对焦炭热性能也有劣化趋势。TD加人配合煤中，不影响配合煤的黏结性及焦炭的冷强度，能明显改善焦炭的热性能。光学组织结构检测表明TD有利于焦炭光学显微组分的各向异
性发展，XRD分析表明TD提高了焦炭的石墨化程度。关键词：硼系化合物；焦炭；热性能；TD
中图分类号：TQ520.6
文献标识码：A
文章编号：1001-3709（2013）04-0005-04
Researchonimpacttocokepropertiesbyaddingboron
homologuestoblendingcoals
Yan TiejunWang GuanghuiShu DafanShi XiaomingZhao LeiZhou Xuan
( College of Chemical Engineering and Technology , Wuhan Univiersity of Science and Technology , Wuhan 430081 , China) Abstract: In this paper,the impact to coke properties by adding boron homologues to blending coals is studied. The result shows that the caking of blended coal and cold strength of coke would get worse as BO,BA and BX are added and the coke thermal properties would also appear degradation trend with adding amount increased. It also indicates that TD added to the blended coal would not impact the coal caking and cold strength of coke but can obviously improve the thermal properties of coke -Coke optical texture test shows that TD can promote the development of coke anisotropy . Furthermore
the XRD analysis shows that TD can upgrade the graphitization of coke . Key words: Boron homologue; Coke; Thermal properties; TD
焦炭在高炉炼铁过程中起着料柱骨架、热源、渗
碳剂和还原剂的作用，是重要的治金能源。焦炭质量的好坏对高炉顺行和高炉冶炼的技术、经济指标具有较大的影响。而高炉大型化及喷煤比的不断提高使焦炭作为料柱骨架的作用尤为重要。因此，改善焦炭的性能，尤其是改善与焦炭骨架作用密切相关的热性能成为当前研究的重点。
目前改善焦炭热性能的方法有配型煤炼焦、干法熄焦、捣固炼焦和煤调湿以及对焦炭进行钝化等。而焦炭的钝化研究主要集中于在湿法熄焦过程中加入硼系化合物及其复配体，即通过焦炭表面液态附着，并且已用于工业生产]。但随着国家对节能环保的日益重视，干法熄焦已在逐渐取代湿法熄焦，因收稿日期：2013-03-26
作者简介：严铁军（1986－），男，硕士研究生
此通过在熄焦水中加入钝化剂来喷洒红焦使钝化剂附着在焦炭表面的方法也将随之淘汰。并且在焦炭表面液态附着方法仅能在焦炭表面分布添加剂，而通过在配合煤中添加的方法，可实现钝化剂在焦炭中的均勾分布，为钝化剂在于法熄焦中的应用开辟了新的路径。本研究将BO、BA、BX、TD作为添加剂加入配合煤中来探索其对配合煤及焦炭质量的影响，旨在找到提高焦炭热性能的新方法，研究其作用机理，为钝化剂在干法熄焦中的应用提供理论基础。
1试验部分 1.1试验原料
试验用配合煤样取自武汉钢铁集团公司焦化公
基金项目：湖北省自然科学基金项目（2008CDB025）、武汉科技大学校基金（2010XZ012）和武汉科技大学绿色制造与节能减排科技研究
中心开放基金（B1014）