橡胶隔振器的静动态特性影响因素试验研究
王文杰，沈建平，梁启明，王志刚，马炳杰
（七一一研究所，上海200090）
摘要：以两种常用的船舶橡胶隔振器为研究对象，通过调整不同的试验条件，进行了隔振器的静态和动态特性试验研究。研究表明：静态性能影响因素按影响大到小，分别为加载速率、预压次数、加载时间间隔；而对动态性能，激励位移的增大或预加载荷的减小，均使得动刚度-频率曲线有整体下降的趋势。
关键调：橡胶隔振器；静动态特性；试验
中图分类号：U661.44
文献标识码：A
文章编号：1001-4357(2012)02003004
Study of the Experiment on the Factors Influencing
theDynamicandStaticCharacteristicsofRubberIsolator Wang Wenjie,Shen Jianping,Liang Qiming,Wang Zhigang,Ma Bingjie
(Shanghai Marine Diesel Engine Research Institute, Shanghai 200090)
Abstract: Research was carried out on two widely-adopted marine rubber isolators. Experiments were done under different conditions to study the static and dynamic performance of these two isolators respec-tively. The experiment results shows that, for static performance, the influencing factors are loading rate, preloading times and loading interval, with the influence decreases in order; whereas for the dynamic per-formance, the dynamic stiffness-frequency curve descends when exciting displacement increases or pre-loading decreases.
Keywords: rubber isolator; static and dynamic characteristics; experiment
0引言
当今船舶领域，主机及其他动力设备的隔振十分重要。采用橡胶隔振器来支撑动力设备和精密仪器是现阶段船舶通常采用的隔振方法，它既可以起到减振降噪的作用，又可起到冲击隔离的作用。
目前大部分隔振器所采用的橡胶材料是一种特殊的合成材料，具有耐久性和可靠性好、易生产和价格便宜等优点，是当前应用最广泛的隔振器材料。然而，橡胶材料的特性也决定了其易受到应用环境和设备振动形式的影响，因此在不同工况或不同使用频率的情况下，隔振器的隔振性能也会有所不同。关于隔振器性能的测试方法，国家标准GB
T15168-94中已经给出了比较详细的规定；而随着试验条件的改变，对结果将有何影响，目前还缺少研究判断。为了更深入研究隔振器的静动态性能，本文通过调整试验条件并在一定程度上突破了国标的限制，观察其对隔振器的静动态特性带来的影响，为以后的试验提供参考。
本文选用目前船舶设备上应用较广泛的某A 型和某B型两种橡胶隔振器（图1），进行了大量的静态和动态特性试验研究。其中，A型为纯压缩型式隔振器，B型为半剪切半压缩型式隔振器，基本参数见表1。根据试验数据分析了两种隔振器的静态特性和动态特性；并通过调整试验条件，来判断这些条件对隔振器特性的影响大小。
收稿日期：2011-1208
作者简介：王文杰（1986-），硕士在读，主要研究方向为：船舶动力装置报动控制，E-mail：verjay@163.com