总第259期 2017年第7期
河北冶金 HEBEI METALLURGY
链篦机一回转窑工艺
配加含铁有机粘结剂试验
杜小军
（河钢集团宜钢公司炼铁厂，河北宣化075100）
Total No. 259 2017,Number7
试验方案。基准试验方案为膨润土配比1.8%；部分代替方案为膨润土0.5%+粘结剂0.6%、膨润土 0.8%+粘结剂0.6%；全部代替方案为粘结剂配加0.9%~1.2%。综合球团矿的各项技术指标，认为膨润土0.5%+粘结剂0.6%的配料方案效果最好
关键词：链算机一回转窑工艺：有机粘结剂；膨润土；球团矿；试验
中图分类号：TF046.6
文献标识码：A
doi:10. 13630/j. cnki.13 1172.2017. 0705
文章编号：10065008（2017)07001905
PLANTTRIALOFADDINGFERROUS
ORGANICBINDERINGRATE-ROTARYKILN
Du Xiaojun
(Iron Making Plant，HBIS Group Xuansteel company，Xuanhau,Hebei,075100）
Abstract : The paper introduces the test plan to use ferrous organic binder to take place of bentonite to produce pellet in the grate rotary kiln of Xuansteel Iron Making Plant. The standard test scheme is bentonite ratio as 1.8% ; partial substitution scheme are bentonite 0. 5% + binder as 0. 6% or bentonite 0. 8% + binder 0. 6% ; all substitution scheme is binder 0. 9% ~ 1. 2% . According to the technical indicators of pellets, it is supposed that the best scheme is bentonite 0. 5% + binder 0. 6% .
Key Words: grate rotary kiln; organic binder; bentonite ; pellet; test
0
引言
为了进一步探索有机粘结剂在球团生产中的使用效果，提高球团矿品位，降低球团矿SiO，含量，改善球团矿冶金性能。2016年10月8~18日，在宣钢炼铁厂2#回转窑球团生产线上再次进行配加含铁有机粘结剂工业试验。其自的一是使用有机粘结剂全部或部分替代膨润土；二是改善球团矿质量，即提高球团矿品位，降低SiO含量，使球团矿的抗压强度、FeO指标、转鼓指数、还原度、低温还原粉化指数、软化区间等指标不低于基准数据，且有改善。以使回转窑球团生产工艺稳定顺行，不出现生球爆裂窑况失常、窑内结块等现象，促进成本降低，有明
收稿日期；201703-25
作者简介：杜小军（1972－），男，工程师，1996年毕业于河北理工学院采矿工程专业，现在河钢集团宜钢公司炼铁厂工作，E-mail： 13933995582@ 163. com
万方数据
显的经济效益。
试验期间工艺、设备及原料情况
1
现有工艺、设备条件
1.1
（1）有机粘结剂不经过干燥工序直接从2#回转窑配料3#膨润土仓配加。
（2）为了保证试验效果，混合料全部经过润磨工序。
（3）根据上次试验经验，在混-4皮带、磨5皮带增设混合料补水点。
(4）造球盘设两路打水管。
其他各部工艺、设备条件不变。
1.2试验原料条件
宣钢球团生产所用铁矿粉主要为高钛半自熔精粉、低钛自熔精粉、近北庄低钛酸精及高品质低钛酸精，膨润土使用钠基土
试验期间主要原料结构：高钛半自熔精粉
19