钛合金化HC700/980CP 冷轧复相钢退火工艺研究
田文波，何方，刘自权
（河钢集团邯钢公司技术中心，河北邯郸056015）
Total No. 260 2017,Number8
00 980CP冷轧复相钢钢带的退火工艺，进行了复相钢连续退火工艺模拟，试验了带速、均热温度、快冷终冷
温度对钢带的抗拉强度和延伸率的影响，确定了HC700/980CP复相钢的最佳热处理工艺。关键词：钛合金化；复相钢；退火工艺；研究
中图分类号：TG156.21
文献标志码：A
doi : 10. 13630/j. cnki. 13 1172. 2017. 0804
文章编号：10065008（2017)08001703
STUDYONANNEALING
PROCESSOFTITANIUMALLOYINGCOLD
Tian Wenbo, He Fang, Liu Ziquan
( Technology Center, HBIS Group Hansteel Company, Handan, Hebei, 056015)
Abstract: In order to get the appropriate continuous annealing parameters, the thermal simulation testing ma-chine Gleeble CAS300 II was used to study the annealing process of cold rolled complex phase HC700/ 980CP steel strip, simulate the continuous annealing process for multiphase steel, investigate the effects of belt speed, soaking temperature and rapid cooling finish temperature on tensile strength and elongation of
steel strip. And the optimum heat treatment technology of HC700/980CP steel is determined. Key Words: titanium alloying; complex phase steel; annealing process; study
引言
目前，汽车车身材料的轻量化已成为发展趋势。
与双相钢相比，复相钢具有较高的屈服强度和高的能量吸收能力，特别适用于要求良好的抗冲击性能的零件（如防撞杆、保险杠和B立柱等安全零件），微观组织主要以贝氏体和（或）铁素体组织为基体，并且通常分布少量的马体、残余奥氏体和珠光体组织。目前国内复相钢基本依赖进口产品，采购成本高昂，实现冷轧汽车板复相钢的国产化可进一步降低国内汽车企业的生产制造成本。为了确定合理的复相钢连续退火工艺参数，在热模拟试验机上进行了1000MPa级钛合金化HC700/980CP复相钢
收稿日期：2017-05-19
作者简介：田文波（1985－），男，助理工程师，2009年毕业于北京科技大学材料科学与工程专业，现在河钢集团邯钢公司从事轧钢工作， E mail : tianwenbo@ mail. hgit. en
万方数据
连续退火工艺模拟，分析了退火温度、时效温度对钢的抗拉强度和延伸率的影响，确定了复相钢最佳的热处理工艺。
1
试验材料与方法
1.1
试验材料
试验材料采用含钛的合金化复相钢HC700/
980CP，在冷硬板上取样，试样尺寸为200mm×600 mm。HC700/980CP复相钢的化学成分见1。
表1HC700/980CP复相钢的化学成分Wt%
Tab.1
Chemical composition of complex steel HC700/980CP wt%
c 0.11
IS ≤0.69
1.2试验方法
Mn 1.18
P
s
Ti
≤0.008
≤0.006
≤0.026
1.2.1热处理工艺试验方案
Als 0.026
试验在河钢钢研院热模拟试验机上进行，热处理工艺试验方案见表2。该复相钢的热处理工艺：
17