总第245期 2016年第5期
河状治金 HEBEI METALLURGY
连铸工艺对齿轮钢铸坏碳偏析的影响分析
郭平
（河锅集团宣钢公司，河北宣化075100）
Total No.245 2016,Number5
摘要：钢液在凝固过程中由于碳的不均匀分布导致了铸坏碳偏析。研究了钢水过热度与拉速、二冷比水量、电磁搅拌强度对齿轮钢铸坏碳偏析的影响。结果表明：拉速控制在1.7m/min，过热度控制在20~ 35℃；结晶器电磁搅拌强度和末端电磁揽拌强度扭矩分别在32N.cm、15N.cm，比水量在0.6L/kg时，连铸坏碳编析改善比较明显。
关键词：齿轮钢；连铸工艺；铸坏；碳偏析
中图分类号：TG142.1
文献标识码：B
doi;10. 13630/j. cnki. 13 1172. 2016. 0504
文章编号：10065008(2016)050015-03
INFLUENCEOFCONTINUOUS CASTINGPROCESSONCARBON
SEGRAGATIONINGEARSTEELCASTINGBLANK
Guo Ping
(Hesteel Group Xuansteel Company,Xuanhua，Hebei,075100)
Abstract: The carbon segregation in casting blank is caused by inhomogeneous carbon distribution in solidification of molten steel. It is researched the influence of molten steel superheating degree, casting speed, specific water flowrate of secondary cooling, clectromagnetic stirring strength on the segregation. It is showed from the result that the segregation gets effective improved when casting speed controlled at 1. 7 m/min,superheating degree as 20 to 35 C, stirring strength and end stirring strength torque separately as 32 and 15 N. cm, specific water flowrate as 0,6 L/kg.
Key Words: gear steel; continuous casting process; casting blank;carbon segregation
引言
在齿轮加工过程中经常会出现芯部的裂纹，这
主要是由于轧材的偏析造成的，虽然在加工和热处理过程中能够减轻但不能彻底消除。轧材偏析级别大小主要是由连铸坏结晶成分不均匀的程度造成的，而铸坏低倍偏析的影响因素主要与钢液成分、浇铸温度、浇铸速度、结晶器冷却速度、电磁搅拌强度有关[1.2]。偏析对于制作的轴类零件会造成非常大
收稿日期：2016-02-16
作者简介：郭平（1981－），男，工程师，2005年毕业于河北理工大学金属材料工程专业，现在河钢集团宣钢公司一钢轧厂从事轧钢生产，
工艺优化与质量管理工作，E-mail；mahuigpp@163.com 万方数据
的缺陷。本文主要针对影响齿轮钢连铸坏偏析的几个主要因索进行了研究，以保证连铸坏的质量。
研究条件和方法
宣钢--钢轧厂100t炉区工艺路线：铁水脱硫一转炉冶炼→LF精炼→连铸机（电搅）。生产的 20CrMnTi连铸坏是在3#连铸机生产的，其设备参数见表1。
15