唐钢烧结配加加拿大精粉生产实践
李旺,甄常亮，周永宁，黄亚玲（河钢集团唐钢公司，河北唐山063016）
Total No. 256 2017,Number4
摘要：在研究加拿大精粉基础性能的基础上，通过工业试验，找出不同加拿大精粉配比对烧结生产过程及烧结矿质量的影响规律，确定加拿大精粉适宜配比为4%。在加拿大精粉配比为4%的配料方案下烧结生产料层厚度由680mm提高到710mm、燃料配比为上限、垂直燃结速度由13.95mm/min降低至
13.21mm/min，烧结矿的转鼓强度提高了0.23%，低温还原粉化率降低0.96%。关键词：烧结；加拿大精粉；实践
中图分类号TF046.4
文献标识码：B
doi: 10. 13630/j. cnki. 13 1172. 2017. 0402
文章编号：10065008（2017)04000604
PRODUCTIONPRACTICEOFADDINGCANADIAN FINEPOWDERINTANGSTEELSINTERINGPROCESS
Li Wang,Zhen Changliang,ZhouYongning,Huang Yaling
(HBIS Group Tangsteel Company, Tangshan, Hebei, 063016)
Abstract : Based on the study of the basic performance of Canada concentrate, the regular effects of different proportion of the Canada concentrate on sintering process and sinter quality were found out through production practice. Finally it was confirmed that 4% of the Canada concentrate used in the sintering is the appropriate proportion. Under this proportion, sintering layer thickness is increased from 680 mm to 710 mm, vertical sintering speed is decreased from 13.95 mm/min 13. 21 mm/min, the drum strength of sinter is increased
about 0. 23 percentage, and the RDI is reduced about 0. 96 percentage. Key Words : sintering; Canada concentrate; practice
引言
随着钢铁产能过剩，市场竞争日趋激烈，钢企要
生存发展，只能靠降本增效，而降低成本的关键在铁前烧结。为了降低烧结配矿成本，充分拓展铁矿石资源，唐钢公司在2015年进口了加拿大精粉，为了确定适宜的加拿大精粉配比，唐钢公司在2015年5 月至7月开展了工业试验研究。
加拿大精粉基础性能
加拿大精粉的化学成分由唐钢炼铁化验室检
测，烧结性能及微量元素电华北理工大学检测，检测
结果分别列人表1、表2和表3。收稿日期；2017-02-19
作者简介：李旺（1983－），男，工程师，2007年毕业于西安建筑科技大学冶金工程专业，现在河钢集团唐钢公司炼铁部从事烧结技术管理工作,Email:liwang1999@163.com
6
万方数据
表1加拿大精粉的化学成分
%
The chemical composition of Canadian fine powder %
Tab.1
TFe 66.12 Alz03 0.52
Tab.2
熔化温度 1508
Feo 11.75 To 0.088
Sio2 4.07 S 010'0
Cao 0.50 P 0.010
2加拿大精粉的烧结性能表2
Mgo 0.31 H20 2.75
Sintering property of Canadian fine powder
最低同化温度
1230
液相流动性
%/ 1.138
最大吸水率
%/ 18.96