总第255期 2017年第3期
河北冶金 HEBEIMETALLURGY
提高棒材生产线
冷床裙板机构耐磨性的实践
董晖
（河钢集团宣钢公司小型轧钢厂，河北宣化075100）
Total No.255 2017,Number3
摘要：介绍了选用耐磨性高的合金材质对棒材生产线冷床裙板机构的输人辑道和裙板进行改造的实践。通过在结构设计上分别选用合金辑环过盈连接和梯形植内镶嵌耐磨合金衬板的形式，仅在受力磨损部位选用耐磨材料，不仅提高了输人辊道和裙板的使用寿命，还节约了改造成本，取得了良好的改造效果。关键词：棒材生产线；输入辑道；制动裙板；耐磨性
中图分类号：TG333.3
文献标识码：B
doi:10.13630/j.cnki.13 1172.2017.0317
文章编号：10065008(2017)03006703
PRACTICETOIMPROVEABRASION RESISTANCEOFAPRONBOARDOF
COOLINGBEDOFBARPRODUCTIONLINE
Dong Hui
(Small Section Steel Rolling Mill, Hesteel Group Xuansteel Company, Xuanhua, Hebei, 075100)
Abstract: The practice is introduced to reform the entry roll table and apron board of cooling bed of bar production line with alloy material of high abrasion resistance: in structure design, selecting separately alloy roll ring interference fitting or inlaying abrasion resistant alloy liner in dovetail groove. These measures, to select the abrasion resistant materials only in the loading and wearing part, do not only prolong the work life
of entry roll table and apron board, but also save reformation cost, so the good effect got. Key Words: bar production line; entry roll table; braking apron board; abrasion resistance
0
引言
在棒材生产线，轧件离开轧线最末架轧机时的速度往往高达18m/s，温度高达900~1100℃，如此高温且高速运行的棒材要通过冷床输人辊道的输送，再经过约200m长的裙板降速制动后，被送上冷床进行冷却，最后进人精整区域整形包装。由于普通的输人辑道和裙板耐磨性差，在高温高速轧件的连续作用下，输人辊道的辊面和裙板的两个斜面上都容易磨出一条凹槽，如不及时更换，很有可能导致跑钢事故，严重影响生产节奏。为此有必要选择一种合适的耐磨材料并进行适当的结构改进以提高输
人辊道和裙板的耐磨性。收稿日期：2017-01-13
作者简介：董晖（1983－），女，工程师，2012年毕业于河北联合大学冶金工程专业，河钢集团宣钢公司小型轧钢厂从事技术管理工作，
Email;meimiumama09163.com 万方数据
提高输入辊道耐磨性的实践 1
冷床输入辑道组紧贴板安装，通常被分为3 段，第2段在速度上是另外两段的过渡段。
在实际生产过程中，成品轧件在输入辊道上的运动是先加速、再匀速、最后降速并制动。高速的成品轧件在辊道上穿行的过程中，它与冷床输入辑辊道之间同时发生滚动磨擦和滑动磨擦，而加剧辊道辊面磨损的主要原因是其中的滑动磨擦。
裙板与辊道安装如图1所示。通常输人辊道的安装轴线与水平面呈12°角，向制动裙板侧倾斜。当输人变频辑道的辊面被磨擦受损后会出现以下两种情况：
(1)磨损造成辊子辊身直径变小，辊面线速度也随之减小，从而使得系统的速度匹配出现偏差。
67