0
总第245期 2016年第5期
河北冶金 HEBEIMETALLURGY
炼钢脱氧新材料钢砂铝的应用
孟庆龙"，汪红有，杨
丽
Total No. 245 2016,Number5
（1.唐山国丰钢铁有限公司，河北唐山063300;2.唐山科技职业技术学院，河北唐山063001）摘要：介绍了唐山国丰钢铁公司炼钢脱氧新材料钢砂铝的生产工艺及理化指标。从实际脱氧效果、铸坏氧氨含量、成本等方面与原脱氧用材料铝铁进行了对比。结果表明，每千克钢砂铝较铝铁多脱氧1.42
Ppm，成本低1.65元/t钢，对铸坏氧氮含量无明显影响，对钢水成分的影响可忽略不计。关键调：钢砂铝脱氧；铝铁脱氧；脱氧效果；成本；对比
中图分类号：TF704.1
文献标识码：B
doi;10. 13630/j. cnki. 13 1172. 2016. 0514
文章编号：10065008(2016)05004802
APPLICATIONOFSTEELALUMINUM,
NEWDEOXIDATIONMATERIALFORSTEELMAKING
Meng Qinglong', Wang Hongyou', Yang Li?
(1. Tangshan Guofeng Iron and Steel Co. Ltd., Tangshan, Hebei, 063300; 2. Tangshan Science and Technology Institute of Vocational and Technique, Tangshan, Hebei, 063001)
Abstract; It is introduced the production process and physical and chemical indexes of steel aluminum, a new deoxidation material for steel making. It is compared with the original ferro aluminum in actual deoxidation effect, oxygen and nitrogen contents in casting billet and cost: in the first item, the former is 1. 42 ppm/kg higher than the later; in the cost, the former 1. 65 yuan/t lower than the latter; the former has no obvious influence on the second item, little effect on molten steel composition.
Key Words; steel aluminum deoxidation; ferro aluminum deoxidation; deoxidation effect; cost; compari-son
引言
国内钢铁行业在经历了几十年的快速发展后，
出现了供大于求的局面。特别是2009年全球经济危机更使这一矛盾凸显，钢铁业道遇了前所未有的挑战。原材料、能源等价格不断上涨，面钢铁产品销售不畅，价格持续下滑，给钢铁企业带来了巨大的生存压力，降低生产成本成为钢铁企业生存和发展的重要任务。
2015年，唐山国丰钢铁有限公司在转炉炉后脱氧环节使用了新材料钢砂铝，并与常用铝铁进行对比，结果表明，单位用量钢砂铝比铝铁脱氧多，且吨钢成本低["]。
生产工艺
收稿日期：2016=0215
作者简介：孟庆龙（1988－），男，助理工程师，2010年毕业于河北理工大学轻工学院冶金工程专业，现在唐山国丰钢铁有限公司从事炼
钢技术工作，Email；WTKKKTW@163.com 48
万方数据
钢砂铝生产工艺：高温铝水（或铝锭熔化后)一→ 保温容器→+铝槽→空气压缩机喷钢砂→水冷池→定尺切割→剪切（每段直径40mm，长度50~60mm） →包装→发货。
铝铁生产工艺：电炉熔化废钢→电炉熔化铝锭 →模铸→空冷[2]。
钢砂铝由于采用水冷池冷却，较铝铁浇铸成型空冷而言，无表面氧化现象。
2
主要理化指标
钢砂铝与铝铁理化指标对比如表1所示。
表1钢砂铝、铝铁理化指标对比 Tab. 1Contrast of steel aluminum and
ferro aluminum in physical and cbemical indexes
物料名称钢砂铝铝铁
Al 82 48
Fe 18 52
%
由表1可知，钢砂铝含铝量较铝铁高，含铁量较