0
总第255期 2017年第3期
河北冶金 HEBEI METALLURGY
汽车转向节盘面结瘤原因分析
胡正伟，高建华，王广利，李双居
（河钢集团石钢公司技术中心，河北石家庄050031）
Total No. 255 2017,Number3
摘要：通过对汽车转向节盘面结瘤体进行宏观、金相、硬度和能谱分析，认为锻造时熔化的氧化铁皮与石墨膏发生反应生成了硬度较高的亚共晶组织结瘤体，是造成钻孔困难的原因。通过降低加热温度、稀释
石墨膏水溶液，加强吹扫等措施，避免了缺陷的产生，并取得了较好的效果。关键词：汽车转向节；氧化铁皮；石墨膏；亚共晶组织；结瘤
中图分类号：TG142.1
文献标识码：A
doi;10. 13630/j. cnki. 13 1172. 2017. 0303
文章编号：10065008(2017)03001504
REASONANALYSISFOR
SURFACESCAFFOLDINGONSPINDLE Hu Zhengwei, Gao Jianhua, Wang Guangli, Li Shuangju
(Technique Center, Hesteel Group Shisteel Company, Shijiazhuang, Hebei, 050031)
Abstract: With analysis in macro observation, metallographic, hardness and energy spectrum for the scaffolding body on the disc surface of spindle, it is considered that the reason to make drill difficult is that the scale melted in forging reacts with graphite grease to produce hypoeutectic structure scaffolding with higher hardness. With measures: reducing heating temperature, diluting water solution of graphite grease, enhancing sweeping, the defect is avoided, good effect got.
Key Words; spindle; scale; graphite grease; hypoeutectic structure; scaffolding
引言
某转向节厂使用40Cr生产汽车转向节，在钻孔
时发现部分转向节下盘面有结瘤，瘤体形状不规则，表面有气孔，硬度比基体高，造成钻中心孔时加工困难，为此对缺陷产生原因进行了分析。
样品分析
1.1生产工艺和缺陷品宏观形貌
1.1.1
生产工艺
锯切下料—中频加热(1100~1150℃）—模具用压缩空气吹扫一喷石墨膏水溶液(1：6)一锻造（平锻和立锻）一淬火（温度850℃，介质为火液）一回火（温度620℃，水冷）一抛丸一钻中心孔一机加工。
1.1.2缺陷品宏观形貌
经过调查缺陷产生在锻造(平锻)阶段，因此选收稿日期：201701-06
作者简介：胡正伟（1987-），男，助理工程师，2010年毕业于河北工业职业技术学院，现在河钢集团石钢公司技术中心工作，E-mail：
sggszly@ 163. com 万方数据
取锻造后的2#样品进行理化检测和高倍分析。缺陷品宏观形貌如图1~3所示。
图1
转向节形貌
Fig.1
1#
Morphology 1 of spindle
15