电泳涂装废水处理技术
曾振国，季献华，苏海娟
（南通京源水工自动化设备有限公司，江苏南通226004）
2011年10月
摘要：叙述了涂装工艺、涂装度水性质以及废水处理技术，指出，废水的成分复杂，排放无规律，水质变化大，废水先经微电解氧化后加药中和况淀，再经AO生化处理，活性炭吸附过滤后出水达到CB8978-1996水综合排放标准中的一级排放标准。
关键词：电泳废水；微电解氧化；水解酸化；接触氧化
中图分类号：X703.1
文献标识码：A
文章编号：2095-0802-(2011)10-0047-02
Electrophoresis'CoatingWastewaterTreatmentTechnology
ZENG Zhen-guo, JI Xianhua, SU Hai-juan
(Nantong Jingyuan hydraulic automation equipment Co., Ltd. Nantong 226004, Jiangsu, China)
Abstract: This paper describes the coating process, coating properties and wastewater treatment technology, pointed out that the complex composition of wastewater, emissions irregular, large changes in water quality, the waste water was dosing and precipitation after the electrolytic oxidation, then after the AO biological treatment, the water reach the level 1 emission standards of CB89781996 standards after activated carbon adsorption filtering-
Key words: electrophoresis wastewater; microelectrolytic oxidation; acidification; contact oxidation
0引言
表面涂装工程是表面工程技术之一，而涂装前处理工艺包括脱脂(除油)等。生产过程中产生大量的污染物仅采用常规工艺不能有效处理废水中树脂、表面活性剂等有机物，很难达标排放，针对上述问题，提出采用废水微电解预处理的工艺形式与传统AO生化处理、活性炭吸附相结合，最终处理后出水达到了一级排放标准的要求。
涂装工艺介绍 1
涂装工艺一般由漆前处理、电泳、清洗和干燥等3 个基本工序组成。
漆前表面处理是涂装工艺的基础，它包括表面清理（除锈、脱脂等)和磷化处理两部分(")。脱脂一般用热碱液清洗和有机溶剂清洗，碱液由强碱、弱酸、聚合碱性盐（如磷酸盐、硅酸盐等)、表面活性剂(阳离子型或非离子型)等适当配合而成。磷化处理是通过化学反应在金属表面形成一层非金属不导电多孔的磷酸盐薄膜，磷化膜可显著提高涂层的附着力、耐蚀性和耐水
收稿日期：2011-08-31
第一作者简介：曾搬国，1982年生，男，江苏建潮人，2005年毕业于扬州大学环境工程专业，工程师。
性。中央空调通风百叶窗磷化一般都采用薄膜锌盐快速磷化处理。磷化液的主要成分是磷酸二氢锌、氧化剂（如NaNO,,NaCIO,)和一些添加剂(如三聚磷酸钠、Na-CI)。磷化处理后一般再进2次~3次水洗。水洗后工件进人涂布电泳工序，目前常用阴极电泳涂装的方法涂装阳离子型水溶型油漆。电冰后用超滤液进行2次~3 次回收水洗，再用去离子水淋洗。面漆一般用三聚氰胺基醇酸树脂磁漆，采用自动喷枪或静电喷漆。喷漆完毕
后通过自动吊具流水线送入烘箱烘干。 2
涂装废水性质 2.1污染源分析
在上述涂装生产过程中，主要由漆前处理废水、电泳废水组成。
前处理废水来自漆前表面处理的脱脂、磷化、表面调整等工序，废水中含有乳化油、表面活性剂、脱脂剂（碱液）、磷化剂（无机盐类）、表面调节剂（无机物）、金属离子、钛白粉、有机溶剂等(2)。
电泳废水主要产生于工件电泳过后清洗过程中工件附着的浮漆及槽液的过程,废水中含有电泳漆（如水溶性环氧树脂、乙醇胺、乙氰酸脂、酚醛树脂等）、颜料（如碳黑、氧化铁红、铅秉等）、填料（如钛白粉、滑石粉等）、有机溶剂（如三乙醇胺、丁醇等）以及少量的金属离子。
以宁波某台资企业电泳废水产生的废水为例，前
47 ·