总第210期 2016年6月
文章编号：10099700(2016)03000803
南方金属 SOUTHERN METALS
X射线荧光熔融法测定锰系合金
中硅、锰和磷含量邢文青，吴超超，王岩，马秀艳（宝钢集团广东韶关钢铁有限公司，广东韶关512123）
Sum.210 June2016
摘要：以过氧化锁为氧化剂，采用X荧光熔融法，对试样进行分段预氧化法处理，建立分析曲线，同时测定锰硅、
锰铁合金中的硅、锰和磷含量，分析结果准确、可靠，满足日常分析要求。关键词：X射线荧光光谱仪；熔融法；锂系合金；含量测定
中图分类号：TC115.22
文献标识码：B
DeterminationofContentsofMn,SiandPinManganese
FerroalloysbyX-rayFluorescenceSpectrometer
XING Wen-qing, WU Chao-chao, WANG Yan, MA Xiu-yan
(Baosteel Group Guangdong Shaoguan iron and Steel Co., Ltd., Shaoguan,Guangdong, 512123,P.R. China)
Abstract : Taking Ba, O, as oxidant, the sample of manganese ferroalloys was decomposed by segmented pre-oxidation treat-ment with X-ray fluorescence spectrometry. The contents of Mn, Si, P contents in manganese ferroalloys could be deter-mined by the XRF method based on standard curve, The results of the samples are aceurate and reliable, and meet the re-quirements of routine analysis.
Key words: X-ray fluorescence spectrometer; fusion method; manganese ferroalloys; content determination
锰硅、锰铁合金是炼钢生产过程中必用原料，不仅用做脱氧剂，更重要的是用来调节钢中合金成分，优化组织结构，进而提高钢铁产品的抗拉、延伸、冲压等物理性能.其化学成分对炼钢过程的质量控制和生产成本有重要影响，因此快速准确地对锰系合金进行检测十分重要.采用传统湿法化学分析，操作繁琐、流程长、耗时耗力，且可能存在人为因素影响目前X荧光光谱法测定锰硅、锰铁中各元素含量多数采用压片法.熔片法因铂-黄金增娲高温下易被合金腐蚀，实际应用鲜见报道.王小武等[1-3]早期提出采用粉末压片X射线荧光光谱法测定锰硅合金主次元素，虽制样简便、快速，但存在样品粒度和矿物效应问题.李京4)提出滴加硝酸对试样进行前处理，克服了矿物效应和粒度效应，但需加入钻内标测定锰，增加了检测成本，陆晓明等3通过离心浇铸制样检测，工艺较复杂，不利于试样批量分析.本文
收稿日期：2016-02-05
通过采用四硼酸锂和碳酸锂混合熔剂对样品进行熔融稀释处理，以过氧化钡为氧化剂，可有效地消除荧光分析中的矿物、颗粒效应的影响，使荧光分析的准
确度满足生产要求 1
实验部分 1.1实验仪器
Axios型X射线荧光光谱仪（荷兰PANalytical 仪器公司）；高频熔样机（北京静远世纪科技有限责
任公司）：铂-黄金埚（P195%=Au5%) 1.2主要试剂
四硼酸锂：分析纯；过氧化钡：分析纯；碳酸锂：分析纯；碘化铵溶液：300g/L
所用试剂如未注明均为分析纯；实验用水均为蒸馏水.
1.3仪器工作条件
各元素测量条件见表1.
作者简介：邢文青（1970－），男，1992年率业于重庆钢铁高等专科学校工业分析专业，工程师