总第172期 2010年2月
文章编号：10099700(2010)01004703
南方金属 SOUTHERN METALS
Sum.172 Fabruary2009
1台300MW机组屏式再热器频繁爆管原因分析
李树学，张启礼
（广东省特种设备检测院，广东广州510655）
摘要：1台300MW锅炉经检修后半年频繁发生爆管，所爆管子均为新换，爆口位置均在焊缝熔合线附近.通过宏观检验、材质分析、金相检验等对屏式再热器管进行分析，结果表明，焊接时，局部出现泽硬的马氏体组织是发生频繁爆管的主要原因，
关键调：爆管；焊缝：金相检验
中图分类号：TK223.3；TG115
文献标识码：B
A failure analysis of the exploded tubes in the platen reheater for a 300 MW boiler
LI Shu-xue, ZHANG Qi-li
( Guangdong Inspection and Examination Institute for Special Equipments, Guangzhou 510655, Guangdong)
Abstract; Explosion frequently occurred with the heat exchange tubes for a 300MW boiler after half a year the tubes were replaced in the boiler overhaul, with the fractures all occurring near the melting line of the welds. Macroscopic examina-tion, material analysis, metallographic characterization showed that the martensitic structure formed due to the local
quenching occurring during welding the tubes was responsible for the tube explosion. Key words: tube explosion; weld; metallographic examination
1简介
广东某电厂1台300MW锅炉于1993年投产
该锅炉为上海锅炉厂生产，型号为SG-1025/18.3 M316，表1为锅炉主要技术参数
表1锅炉主要技术参数
额定蒸发量/·b-
1 025
再热器出口工作盟度/℃
541
燃料种类山西雁北烟煤
循环方式强制循环
再热器进口工作压力/MPa
3.86
燃烧方式过热器出口工作压力/MP过热器出口工作温度/C再热器出口工作压力/MP
3.65
四角切圆微烧
18.3
541
再热器进口工作温度/℃
323
2008年2月检修后更换了部分屏式再热器管到2008年8月后，屏式再热器接连出现爆管，所爆管子均为新换，爆口位置均在焊缝熔合线，爆管前运行情况正常，没有超温超压现象
2
屏式再热器管爆口的宏观形貌
屏式再热器材质为12CrlMoVG，规格D63mm
x4.1mm，图1为所截取的原始暴漏的管子，图2
为爆漏管焊缝处裂纹的放大图，收稿日期：2009-07-16
基金项目：广东省安全生产基金项局（2008-79-C）
锅筒工作压力/MPa
19.67
给水压力/MPa
20.1
图1所截取的暴漏的管子
作者简介：李树学（1961－），男，1983年毕业于式汉水利水电学院焊接专业，高级工程师，
给水温度/℃
282