总第212期 2016年10月
文章编号：10099700(2016)05000104
南方金属 SOUTHERN METALS
Sum.212 October2016
Fe-6.5Si软磁合金粉末制备工艺方法的研究
陈远星，刘志坚
（广东省钢铁研究所，广东广州510640）
摘要：通过添加适当含量的磷元素，解决用机械破碎法制备Fe-6.5Si软磁合金粉末的难题.分别采用普通球磨、环链磨和六角球磨等工艺实验方法进行制备Fe-6.5Si软磁合金粉末研究.结果表明，在同等条件下，六角球磨工艺方法的制粉效率较高，粉末形貌特征和电磁性能均较佳
关键调：Fe-6.5Si软磁合金；机械破碎；制备工艺；制粉效率；粉末形貌特征
中图分类号：TG132.2*71
文献标识码：A
StudyonthePreparationMethodofSoftMagneticAlloyPowderFe-6.5Si
CHEN Yuan-xing, LIU Zhi-jian
(Guangdong Iron and Steel Institute, Guangzhou, Guangdong, 510640, P. R. China)
Abstract : By adding proper content of phosphorus, the problem of preparing soft magnetic alloy powder Fe 6. 5Si by me chanical crushing is solved. The soft magnetic alloy powder Fe 6. 5Si is prepared by ordinary ball milling, ring grinding and six angle ball milling respectively. The results show that, under the same conditions, the efficiency by six angle ball milling is higher, the powder morphology and electromagnetic properties are better than the others.
Key words: soft magnetic alloy Fe 6. 5Si; mechanical crushing: preparation technology; milling efficiency ; powder mor phology characteristies
0引言
Fe-6.5Si软磁合金具有优异的软磁性能，是高频电机铁芯的理想材料.它不仅有希望替代菩通硅钢片用于高频电机铁芯，面且还可广泛用作音频和视频磁头材料以及卡片阅读器用磁头材料(1-2].迄今为止，硅含量约为6.5%的Fe-Si软磁合金已经在变压器、转换器和高频掘流线圈中得到广泛应用[3]
众所周知，随着材料中Si含量的增加，尤其超过5%以后，由于B，或DO,（Fe,Si)有序相的出现， Fe-Si合金变得既硬又脆，冷加工性能急剧恶化，因而很难通过常规的轧制方法制备[4]，通过粉末冶金方法制备出Fe-6.5Si合金粉，并在其表面包覆一层绝缘材料，经过成型直接制造成软磁合金粉芯，既可以保证6.5%Si高硅合金粉的高磁感，所包覆的绝缘材料又起到提高电阻率、降低高频涡流损失
收稿日期：201606-13
基金项目：广东省省级科技计划项目（2014B070706032）
的作用.另外用粉末冶金工艺制作软磁合金粉芯，还可省去轧钢和冲片叠装等成型工艺，使材料利用率得到很大的提高.本文对Fe-6.5Si软磁合金粉末
的不同制备工艺方法进行实验研究 1实验
1.1实验的工艺流程
实验的工艺流程为：原材料准备－配料-冶炼铸锭一成分分析-铸锭-破碎-制粉一筛分-热处
理-混料-包覆一烧结-性能检测 1.2合金材料制粉实验过程
Fe-6.5Si软磁合金材料采用不添加微量元素和添加微量磷元素分别进行制粉实验.入料为粒度均在-80目以下Fe-6.5Si合金粗颗粒，分别采用普通球磨、环锤磨和六角球磨等实验方法制备粉末，其中六角球磨工艺采用本所自制的六角球磨机进
作者简介：陈远星（1973－），男，1996年毕业予昆明理工大学钢铁冶金专业，高级工程师。