第37卷第6期 2015年12月
文章编号：1001—5108(2015)06—0060—05
四川冶金 Sichuan Metallurgy
再生塔衬里的焊接工艺
朱宁，昊刚，郭永春
（攀钢集团工程技术有限公司，四川攀枝花617000）
Vol. 37No. 6 Dec.,2015
摘要：通过对炼铁厂再生塔254SMo不锈钢衬板的性能进行分析，针对在腐蚀性环境使用的情况，选择合适的焊接方法及相对应的焊接材料，采取搭接接头和塞焊缝方式，制定出合理的爆接工
艺和措施，保证了254SMo不锈钢衬板的安装焊接质量和使用性能要求。关键词：254SMo不锈钢；腐蚀；焊接
中图分类号：TG457
文献标识码：B
WeldingTechnologyofRegeneratingColumnLining
ZHUNing，WUGang,GUOYong-chun
(Pangang Group Engineering Technology Co., Ltd., Panzhihua Sichuan 617000)
Abstract: Aiming at the performance for the corrosive environment, this paper selected the suit-able welding method and the corresponding welding materials,applied the overlap joint and plug weld methods and formulated the reasonable welding technology as well as the countermeasures so as toguaranteetheerectionwelding quality and performance requirements of 254SMo stainless lining board by analyzing the performance of 254Mo stainless lining board of regenerating column in theiron making plant.
Key words: 254SMo; stainless steel; corrosion; welding
1引言
攀钢烧结工序中产生的烟气含有大量的
氯化物、硫氧化物、氨氧化物等腐蚀性较强的成分，由于这些腐蚀性物料的作用，烟气脱硫工序原使用316L材质的钢材制作设备，使用不到3个月就发生腐蚀穿透的情况，必须停产更换。为提高脱硫塔设备衬里的使用寿命，保证生产正常运行，决定采用耐蚀性强的 254SMo不锈钢代替316L不锈钢用于再生
塔、脱硫塔等设备衬重。
254SMo是一种高强度（比316L钢的强度高50%）、高韧性的奥氏体不锈钢。具有较高的含氮量，主要用于强腐蚀环境中，有较高的耐点腐蚀和耐缝隙腐蚀性能，优秀的耐晶间腐蚀能力；它还具有很高的延展性和冲击强度及较好的可焊性。但是在焊接过程中，如果焊接工艺和措施不正确，极易造成组织粗大、成分偏析和焊接变形，导致耐腐蚀性能下降等，达不到使用要求。
作者简介：朱宁，焊工高级技师、国际焊接技师，主要从事焊接工艺及焊接培训等方面的工作。