第37卷第2期 2016年4月
·失效分析，
热处理技术与装备
RECHULIJISHUYUZHUANCBEI
热轧带钢头部氧化铁皮的影响因素研究
关建辉，丁美良，孙林
（江苏省沙钢钢铁研究院有限公司，江苏张家港215625）
Vol.37,No.2 Apr,2016
摘要：通过实验室缺陷样品分析，生产数据统计，分析了影响热轧带钢头部氧化铁缺陷的因素。结果表明：中间坏头部温度高是形成头部氧化铁皮的主要因素，轧制计划编排、带钢的化学成分和除辨
状况等也会影响到头部氧化铁皮缺陷的产生。关键词：热轧带钢：头部：氧化铁皮：中间坏
中图分类号：TC335.5文献标志码：A文章编号：1673-4971(2016)02-0036-03
Study of InfluenceFactors onOxide Scale inthe Head of Hot-rolled StripSteel
GUAN Jian-hui, DING Mei-liang, SUN Lin
(Institute of Research of Iron and Steel, Sha-steel, Zhangjiagang Jiangsu 215625, China)
Abstract : The factors influencing oxide scale in the head of hot-rolled strip steel were analyzed by analysis of defect sample and statistics of site data. The result shows that the main factor formed oxide scale defect is higher head temperature at head of intermediate billet, and the arranging hot rolling plan, chemical composition of strip steel and condition of descaling etc. can also affect on generation of oxide scale in the head.
Key words:hot-rolled strip steel; head;oxide scale; intermediate billet
氧化铁皮的问题一直是影响热轧带钢表面质量
的重要方面。热轧过程中，带钢氧化铁皮的影响因素较多，热轧工艺、计划编排、带钢化学成分、设备状况异常等均可能产生氧化铁皮。因此，热轧产品出现氧化铁皮时，需全面排查氧化铁皮形成的原因，针对性制定相应解决措施，从而保证产品表面质量，提高经济效益。
某钢厂1700mm热轧生产线生产SPHC等低Si 钢种出现头部氧化铁皮，缺陷主要出现在钢卷头部 100~150mm位置，缺陷宏观形貌如图1所示。缺陷出现造成钢卷切头长度增加，降低了成材率。国内其他钢厂也存在此类问题，还成立项目攻关组对其进行调研分析1-3)。不同钢厂设备工艺不同，头部氧化铁形成原因及控制措施也不同，头部氧化铁
收稿日期：2015-09-18
皮出现后，进行了实验室缺陷样品分析、工艺参数分析、现场生产状况排查。并讨论热轧各工序对氧化铁皮的影响。
图1头部氧化铁皮的宏观形貌
Fig. 1Macrocosm appearance of oxide scale at head of strip steel
作者简介：关建辉（1985-）男，硕士，助理研究员，主要从事带钢表面质量及组织性能控制研究。
联系电话：15962340612;E-mail：guanjh847126.com
万方数据