第33卷第5期 2012年10月
热处理技术与装备
RECHULI JISHU YU ZHUANGBEI
消除低铬白口铸铁铸造缺陷的措施
李启
（冀中能源机械装务公司石家庄工业泵厂有限公司，河北石家庄050100）
Vol.33,No. 5 Oct,2012
·工艺研究
摘要：本文对低铬白口铸铁材料的缩松、气孔、夹渣及热裂等铸造缺陷进行原因分析，通过改进铸造工艺参数、净化铁水、控制原材料等措施，基本解决了低铬白口铸铁的铸造缺陷问题，可以在一定范围内进行推广应用。
关键词：低铬白口铸铁；铸造缺陷；改进措施
中图分类号：TG252文献标识码：B文章编号：1673-4971(2012)05-0005-03
The Measurefor Eliminating CastingDefects of Low CrWhiteCast Iron
LI Qi
(Shijiazhuang Industry Pump Factory Co. , Lid. ,Shijiazhuang Hebei 050100,China)
Abstract: In this paper, the cause of casting defects in the low Cr white cast iron material such as shrink-age, porosity, slag and hot crack was analyzed. Through improving casting process parameters, purifica tion of the molten iron, controlling of the raw material etc, casting defects of the low Cr white cast iron
were basically resolved, and the above measures can application and extension in a certain range. Key words: low Cr white cast iron;casting defects;improvement measures
0前言
渣浆泵（灰浆泵）是用来输送含有固体颗粒浆体的专用设备。泵体过流部件在运动过程中受到浆体的冲刷，如叶轮、泵壳等的材料应具有一定的抗磨损性能。浆体的介质工况复杂，按颗粒的特性和浓度，可将浆体分为强磨损、中磨损和轻磨损三类。为了提高材料的性价比，针对氧化铝厂等的工况介质情况，我们试验了中损的低铬白口铸铁材料。
低铬白口铸铁材料主要是有较高的碳含量和一定的铬含量，材料的主要成分含碳量2.5%~3.5%，含铬量1.0%~3.5%。铸件成型后，为了满足机械加工要求，进行退火处理，硬度控制在32~42HRC，材料在退火后基体为珠光体，其上分布着白色部分为断网状渗碳体，金相组织如图1示。
在试制过程中，由于此范围的低铬材料铸造工收稿日期：2012-0417
艺性差，生产的铸件存在诸多的缺陷，如缩松、气孔、夹渣并时有热裂纹产生。本文结合铸件的试制过程，对缺陷的原因进行分析，并提出了解决缩松、气孔、夹渣和热裂纹等缺陷的改进措施。
铸件缺陷的原因分析 1
1.1缩松的原因及分析(1-3]
低铬材料出现缩松的部位主要在叶轮的轮毅。叶轮轮体破坏后，宏观观察轮毅周围有大量的缩松，由于此处的壁厚相差较大，认为是热节缩松。因为金属液浇人铸型后，铸件一且形成“容积式凝固的固体外壳”，也就是缩孔形成的开始。如果不形成容积式固体外壳，就不会形成缩孔。
缩松的形成是由于铸型内合金的液态和凝固收缩大于外壳固态收缩，同时在铸件最后凝固的区域
作者简介：李启（1972－），男，高级工程师，主要从事金属材料转造、热处理技术及相应的管理工作。
联系电话：13931112776;Email：lqhb1972@126.com
万方数据