第38卷第1期 2017年2月
热处理技术与装备
RECHULI JISHUYU ZHUANGBEI
Vol.38,No.1 Feb,2017
·工艺研究·
敏化处理对304不锈钢板晶间腐蚀的影响
丰玉玺，陈丽芳，陈安源，许万剑，刘斌（国家不锈钢制品质量监督检验中心，江苏泰州225721）
摘要：对经固溶处理的304不锈钢板进行不同时间的敏化处理实验，电解腐蚀后研究敏化时间对 304不锈钢耐蚀性的影响。通过分析发现随着敏化时间的延长，腐蚀沟的宽度越大，腐蚀程度越重，
说明析出的（CrFe）nCe型碳化物越多，造成晶界贫铬，降低了材料耐蚀性。关键词：不锈钢；晶间腐蚀；敏化处理
中图分类号：TG172.6文献标志码：A
文章编号：1673=4971(2017)01-0015-03
Effect of Sensitizing Treatment on Intergranular Corrosion of
304 Stainless SteelPlate
FENG Yu-xi, CHEN Li-fang,CHEN An-yuan,XU Wan-jian,LIU Bin
(National Stainless Steel Products Quality Supervision and Inspection Center,Taizhou Jiangsu 225721,China) Abstract: The sensitizing treatment experiment is carried out for 304 stainless steel plate after solution treatment at different time. The effect of sensitizing treatment time on corrosion resistance of 304 stainless steel is studied after electrolytic corrosion. The results show that with the increasing of the sensitizing treat-ment time, the heavier width of the corrosion groove, the greater degree of corrosion. The results indicate that the more ( CrFe)a C, carbide precipitated cause the poorer chromium at the grain boundary which de-creases the corrosion resistance of material.
Key words : stainless steel;intergranular corosion;sensitizating;treatment
奥氏体不锈钢晶间腐蚀简述 1
晶间腐蚀指的是材料腐蚀过程沿着晶界进行[1]，造成晶粒间的结合力降低，从而造成材料的强度下降(2]，当材料发生晶间腐蚀时仅通过材料外在观察是很难预判的，因此它带来的破坏往往是非常恶劣和突然的。材料产生晶间腐蚀归根结底主要是材料内部存在不均衡的电化学位，产生电化学腐蚀。晶间腐蚀的机理主要有以下两种：第一种是贫铬理论，主要是指材料经过一定时间的敏化处理，在晶界上析出（CrFe）C。型碳化物，造成晶界及其附近区域贫铬，降低了材料的耐蚀性，贫铬理论是不锈钢晶
收稿日期：2016-09-22
间腐蚀中认可度较高的理论[3-4]第二种是第二相析出理论，该理论认为产生晶间腐蚀的主要原因是晶界出现有害α相，它是一种Fe与Cr形成的金属间化合物，该理论主要用来解释超低碳不锈钢的腐蚀机理4)。两种理论通过大量的实验得到验证，目前能够比较好地解释不锈钢的晶间腐蚀机理。201、 202、301、304、316等奥氏体不锈钢的晶间腐蚀主要是由于含铬碳化物析出引起晶界附近区域贫铬，耐蚀性下降引起的。
工理（801861）
联系电话：18861055628;E-mail;fengyu0822@163.com