扫描振动探针对焊接304L奥氏体不锈钢的敏化行为研究
黄发，胡凡，周庆军
（宝山钢铁股份有限公司研究院，上海201900）
摘要：焊缝等特殊材料结构的敏化会导致其耐晶间腐蚀和晶间应力腐蚀性能降低，传统的双环电化学动电位再活化法(EPR)不能准确地检测出焊材料的敏化信号，从而做出未发生敏化的错误判断，给材料的使用带来风险。采用担描振动探针(SVP)的方法很好地解决了这一难题，成功地检测到窄焊缝区域的敏化特征。
关键词：焊缝；敏化；扫描振动探针
中图分类号：TG172文献标志码：B文章编号：1008-0716(2016)01-0023-05 doi;10. 3969/j. issn. 1008 0716.2016.01.006
Studyon sensitizationbehaviorof weldedtype304Laustenitic stainless
steelusingscanningvibratingprobe HUANGFa,HUFanandZHOUQingjun
(ResearchInstitute,BaoshanIron & Steel Co.,Ltd.,Shanghai201900,China）
Abstract: Sensitization of special structures like weld seams reduces the resistance of materials
23
to intergranular corosion and intergranular stress corrosion cracking. However, the degree of sensitization in these seams could not be detected by the traditional electrochemical potentiokinetic reactivation( EPR) measurement using the double loop method. Results based on non-effective tests bring risks to the application of materials. The problem is solved by scanning vibrating probe(SVP), which successfully detected the sensitization signals of the narrow weld seams.
Key words:weld seam; sensitization; scanning vibrating probe
对耐蚀合金进行热处理（包括焊接等）会使得材料组织中出现微小的颗粒析出物，如304不锈钢中的碳化铬和双相不锈钢中的相（FeCrMo)等。微小颗粒物析出时，其邻近区域若得不到基体中合金元素的扩散补充，就会使该区域元素贫乏，即发生敏化。材料中发生敏化的区域耐晶间履蚀性能教差，也容易发生点蚀和晶间应力腐蚀开裂[1-3]，且其耐蚀性能下降的程度通常取决于合金元素的贫乏程度和贫乏区域的密度。鉴于热处理敏化对材料耐蚀性能的降低，需要一种简单有效的试验方法来快速判定合金中潜在的有害热效应。
黄发博士1985年生2013年毕业于中国科学院金属研究
所现从事金属离蚀与防护电话26649556 E-mailhuangfa@ baosteel, com
目前，实验室主要采用双环电化学动电位再活化法（Electrochemicalpotentiokinetic reactivation measurement，EPR)测试材料的敏化特征[4]，该方法在实验室敏化样品和经热处理发生合金元素贫化的大块样品上取得了较好的测试结果。然而， EPR法得到的是针对材料整个测试区域的综合信号，对于焊缝等特殊材料结构，由于沿融合线的敏化区分布可能是非均匀的，且焊缝热影响区在宏观尺寸上相对基材较小，窄焊缝区域的敏化信号会被大块基材信号中和减弱甚至覆盖，因此采用EPR法较难得到焊缝热影响区的准确敏化信息。而焊接结构在钢铁构件的使用中非常普遍，焊缝区域的敏化问题与危害性也较为突出，如何准确地检测并评价焊缝的敏化程度是研究工作的重点。