第32卷第4期 2011年8月
热处理技术与装备
RECHULI JISHU YU ZHUANGBEI
接续器基体复合强化研究
董茗，郑小民2
Vol. 32,No. 4 Aug，2011
·工艺研究·
(1.南昌轨道交通公司，江西南昌330038；2.江西机械科学研究所，江西南昌330002）
摘要：通过研究接续器的形状特点及使用要求，确定了形变时效复合强化工艺方案，并通过实验对形变量与强化量的关系进行研究，取得合理的工艺参数，最终批量生产出合格的，具有高导电、高强
度钢合金接续器坏件，为后续生产带来极大方便。关键词：形变；时效；复合强化
中图分类号：TC156.93
文章编号：16734971(2010)04000504
文献标识码：A
ResearchonCompoundingStrengthenfortheMatrixofConnector
DONG Ming,ZHENG Xiao-min
(1 ,Nan Chang Rail Transit Co. ,Lad. , Nanchang Jiangxi 330038, China; 2、Jiangxi Province Mechanism Institude, Nanchang Jiangxi 330002, China)
Abstract: A process plan of deformation-ageing compounded strengthening of the connector is determined by studying its shape characteristics and operating requirement. We research the relationship of deforma-tion and intensification by experimention and obtain the reasonable parameters, In the end, we have pro duced the qualified batch copper alloy connector with high electrical conductivity and high strength, which
bring a great convenience for the subsequent production. Key words: deformation; ageing; compounded strengthen
0
引言
如图1、图2所示为电力机车动力电缆接续器的零件图，零件材料为HT铜合金，该合金是一种含稀土的高导电、高强度铜合金。接续器是电气化铁路接触电网接触线的连接装置，工作时要承受很大的张力和电流载荷，并受到机械冲击、电流冲击和机板磨损。因此，接续器要有很高的强度，同时又要具备很好的导电性及较高的软化温度。接续器主要由线夹板与线夹头两部分构成，外形复杂，采用普通加工手段费工费时，且质量难以得到保证。
鉴于以上对零件特点及制造难度和使用要求的分析，我们决定采用形变时效复合强化工艺，通过实验手段对形变量与强化量的关系进行研究，从形变
收稿日期：20110331
量、形变温度、毛坏尺寸、形变速度、润滑剂等方面对 HT铜合金的形变强度影响进行研究，并获取合理工艺参数。最终批量生产出合格的高导、高强度铜合金接续器坏件。
接续器还体成形工艺方案 1
针对电气化铁路动力电缆接续器，江西省科学院应用物理研究所新研制了一种含有稀土的高导高强度铜合金HT铜合金。该合金可通过时效和冷塑性形变提高强度，同时合金的导电率也损失较小。
HT铜合金是面心立方结构的金属材料，层错能较低，从理论上讲此类材料的加工硬化速率必定较高，可通过冷塑性形变来提高强度，但塑性也会下
作者第介：董茗（1965-），男，工程师，主要从事机电设备及模具研究。