薄壁齿轮渗碳淬火畸变的分析与改进
邓影洲
（陕西秦川机械发展股份有限公司热处理厂，陕西宝鸡721009）
Vol.34,No.4 Aug,2013
·工艺研究·
摘要：畸变量主要受零件形状的影响，薄壁齿轮渗碳火后时变量大，简化零件形状可减小畸变量。通过两次正火、降低缓冷出炉温度，考虑工装与零件冷却时热容量的相互影响，将工装和零件作为一个整体考虑并关注零件的冷却速度，分析改进热处理工艺，实现有效控制畸变量的目的。
关键词：形状；畸变量；两次正火；热容量；冷却速度中图分类号：TG157文献标志码：A
文量章编号：1673-4971(2013)04-0019-03
AnalysisandImproveonDistortionforCarburized
and Quenched Thin Gear
DENGYing-zhou
(Heat Treatment Factory of Shanxi Qinchuan Machinery Development Co., Lid. , Baoji Shanxi 721009,China) Abstract: The amount of distortion is mainly influenced by the shape of a part, so the amount of distortion is large after carburized and quenched. The amount of distortion is decreased by changing the complicated shape to simple shape. After adopting twice normalizing, decreasing unloading temperature, considering the mutual effect of parts and fixtures' thermal capacity, and focusing on parts cooling speed during cooling process while considering parts and fixtures as a whole, the amount of distortion is controlled efficiently by analysing and improving heat treatment process
Key words; shape; amount of distortion;twice normalizing ;thermal capacity ;cooling speed
大型柴油发电机是应急条件下对重要装备供电的应急设备，要求具备极高的运行可靠性；而传动齿轮是重要的部件，故该传动齿轮必然也要求具备极高的可靠性。有效地控制畸变，保证齿轮在后续加工工序中能均匀磨齿，获得相对均匀的齿面硬化层，保证齿轮的机械性能。近年来，公司齿轮传动厂承接了大型柴油发电机传动齿轮。由于该齿轮属薄壁件，在渗碳、淬火后出现了较大的畸变。通过热处理工艺的改进，有效地控制了齿轮的畸变量，保证了零件顺利交付使用。
收稿日期：2013-04-03
1齿轮加工工艺流程及技术要求
图1为20CrMo钢发电机传动齿轮的简图，模数 m=8，齿数z=120。工艺流程为：锻件正火→+粗车→ 精车→滚齿→渗碳淬火→车齿顶→车内孔一→低温时效-+钻小孔、磨齿。热处理技术要求：齿面硬度660 ~800HV；放磨后硬化层深2.4~2.9mm，马氏体+ 残余奥氏体≤3级，心部铁索体≤4级；金相组织按 JB/T6141.3-1992《重载齿轮渗碳金相检验》评级。检测随炉处理的Φ56mm×120mm试块：抗拉强度 ≥770MPa；届服强度≥460MPa。