某圆锥滚子轴承故障分析
张伟男，洪杨，刘峰
Vol.38 No.1 Mar.2017
（1.哈尔滨轴承集团公司制造技术部，黑龙江哈尔滨150036；哈尔滨哈轴精密制造有限公司，黑龙江哈尔滨 150036)
摘要：某圈锥滚子轴承用于某种货运汽车的轮毅上，运行40km后，出现轴承抱死、主轴退火、滚子和套圈
变色破损等现象。经过敬障特征、金相组织分析发现，轴承在使用过程中由于安装不当导致轴承失效。关键词：圆锥滚子轴承；轴承失效；粘着磨损；游隙
中图分类号：TH133.33*2
文献标识码：B
文章编码：16724852（2017）01001902
Failure analysis on a tapered roller bearing
ZhangWeinan',Hong Yang,Liu Feng
(1.Manufacturing Technology Department,Harbin Bearing Group Corporation, Harbin 150036, China; 2. Harbin Hazhou Precision Bearing Manufacturing Co., Ltd., Harbin 150036, China )
Abstract: A tapered roller bearing is applied on wheel hubs of some freight trucks.Failure appears with bearing locked,wheel shaftannealed,rings and rollers discolored and damaged after running for 40 kilomiles.Through observational check and microstructure analysis on failure parts,it is found that the failure reasons are the bearing improperly mounting in use.
Key words: tapered roller bearing, bcaring failure, adhesive wear, clearance 1前言
某圆锥滚子轴承用于某特种汽车有限公司制造的货车轮毂毅上，在装配到车辆上运行40km 时，出现轴承抱死，主轴退火，滚子、套圈变色破损，保持架断裂失效。故障轴承返回，对故障轴承进行了分析，并找出轴承失效原因，采取措施避免此类问题的发生，进而保证轴承的使用寿
命。
故障件描述 2
故障轴承损坏严重，内、外圈变色破损且滚道有大量材料堆叠，保持架断裂缺失，内圈大挡边外翻，外径有明显滑动痕迹，滚动体磨损严
重。（图1~图4） 3故障浅析
根据GB/T24611-2009/IS015243:2004《滚动收稿日期：2017-03-03.
作者简介：张伟男（1989-），男，助理工程师，万方数据
图1外圈滚道及窄端面处粘接铁屑图2内圈滚道表面粘接铁屑
轴承损伤和失效术语、特征及原因》的规定，判定该轴承的失效模式为磨损失效。磨损是指在使用过程中，两个滑动或滚动/滑动接触表面的