第34卷第3期 2014年9月
化学传感器 CHEMICALSENSORS
择性电极研究
刘新露*张英
(四川理工学院化学与制药工程学院，四川自贡643000)
Vol. 34, No. 3 Sept .2 01 4
摘要：以碳纳米管-氨基硫脲复合物为载体制成碳糊电极，该电极对铁离子具有选择性的Nernst电位响应，其线性范围为3.5×10-7~1.0×10-mol/L，斜率为30.7mV/decade，检测下限为1.0×10-mol/L。该电极对
Fe*的响应时间为15s,其选择性良好，并能成功应用于Fe*的回收率实验。关键词：多壁碳纳米管：氨基硫脉；Fe“：离子选择性电极
Studyonacarbonpasteiron(l)-selectiveelectrodebasedonthe composite of carbonnanotube-thiosemicarbazide as the carrier
Liu Xin-lu',Zhang Ying
(College of Chemistry and Pharmaceutical Engineering, Sichuan University of Science and Engineering,
Zigong 643000, China
Abstract: A new modified carbon paste electrode based on the composite of carbon nanotube thiosemicarbazide a the carrier was prepared. The electrode exhibits a selective Nernstpotential slope of 30.7 mV/decade for Fe* over a linear range of 3.5 × 10-7~1.0x10-' mol/L. The detection limit of the electrode is 1.0 ×x 10-′ mol/L. The response time
of the electrode is 15 s. The electrode shows a good selectivity for Fe3+ and it can be successfully applied to the recovery of determination of Fe*
Key words: multiwalled carbon nanotube; thiosemicarbazide; Fe't; ion-selective electrode
改善分析测试的灵敏度[5~7]。
0引言
碳糊离子选择性电极是将导电性的石墨粉、
增水性的粘合剂(石蜡油)以及离子载体混合均匀后填充入电极管中而制成的一类电极，碳糊电极具有阻抗低、制备简单、操作简便、反应稳定等优点，逐步成功应用于离子选择性电极的研制中[1~4]。碳糊离子选择性电极的研制关键在于敏感离子载体的研究与开发，碳纳米管作为新型纳米材料，具有良好的导电性能和极大的比表面积，其端面基易于修饰上氨基、羟基、筑基等基团，这些基团易于与金属离子配位结合，将其应用于离子选择性电极敏感载体的研究中将大大
该文将羧基化的多壁碳纳米管通过偶联剂与氨基硫脲超声共混制成纳米复合物，该纳米复合物含有大量的氢基和硫羰基，易与铁离子配位，以此纳米复合物为敏感载体制备出碳糊铁离子选择性电极。研究结果表明该电极对Fe具有优良的能斯特(Nernst)电位响应性能以及良好的选择性。
实验部分 1
1.1主要仪器、药品
217型双盐桥饱和甘汞电极（上海康宁电光技术有限公司),PHS-3C型酸度计(成都世纪方舟
基金项目：绿色催化四川省高校重点实验室项目(LYJ1305)；四川理工学院科研基金项目(2010XJKYL004)*通讯联系人，Email:pxhlxl@126.com