低温辐射金属电热膜的研发
曹体样
（哈尔滨新阳物业管理服务中心，黑龙江哈尔滨150076）
摘要：针对目前低温辐射金属电热膜产品复合不牢、性能不稳定、安装性差的缺点，对其制造的关键技术进行了研究和试验，提出了各生产工序的技术要点，改进了部分生产工艺，完善了生产工艺流程。研制出性能稳定，易于安装的新型金属电热膜。
关键词：电热膜；工艺流程；复合中图分类号：TK11：
文章编号：1009-3230(2011)01-0032-03
文献标志码：
Development ofaNewTypeLowTemperatureRadiant
MetalElectricHeatingFilm
CAO Ti-xiang
(Xinyang Estate Management Service Center of Harbin,Harbin150076,China)
Abstract:Aimed at weak compounding,unstable functions and difficult installation of low temperature radiant metal electric heating film, investigation and test were done on its key technology of manufacture. Main points of working procedure were put forward. Some producing techniques were improved and changed; meanwhile its flow was perfected. A new type metal electric film with stable performance and easy installation was developed.
Key words:Electric radiant heating film; Producing technique flow; Compound
近年来，低温辐射电热膜在建筑、工业、农业、
军事、家庭用品等领域都得到了广泛的应用。特别是在建筑采暖方面"），由于低温辐射电热膜采暖系统存在着节能、节水、节地、安全可靠、卫生环保、寿命长、免维护等诸多优点，因此不仅得到了非常广泛的应用，而且实践证明其应用效果良好[2-4] 。
早期的低温辐射电热膜是以导电油墨作为电阻发热体通电加热产生红外辐射的。由于导电油墨性能存在着局限，特别是长时间使用容易出现发热不匀、老化、龟裂等问题，因而制约了电热膜的应用和发展。为了克服这些缺点，以金属合金取代导电油墨作为电阻发热体的金属电热膜产品收璃日期：201012-10
0修订日期：2010-12-25
作者简介：曹体样（1967－），男，主要从事供热设计管理
工作。
万方数据
得以问世。由于国内生产技术不理想，产品存在差复合不牢、性能不稳定等缺点，特别是复合技术与国外有较大差距，而且国内外的金属电热膜产品存在着现场安装不方便的问题，因此有必要对低温辐射金属电热膜的生产技术和工艺做进一步研究。
新型低温辐射金属电热膜的生产 1
工艺
1.1原材料选择
要生产高性能的低温辐射金属电热膜，材料的选择至关重要，它严重地影响电热膜的质量、性能以及安全可靠性。
(1)绝缘薄膜的选择。绝缘薄膜应选择表面张力较大的阻燃聚酯薄膜，聚酯薄膜的厚度应该在50~100μm左右。