第40卷第5期 2010年5月
涂料工业
PAINT & COATINGS INDUSTRY
水性防火涂料配方研究
林红岩，王春财”，杨鸿伟”
Vol. 40No.5 May2010
（1.大庆石油学院，黑龙江大庆163318;2.大庆龙化新实业总公司，黑龙江大庆163714）
方优化，对该涂料的理化性能和防火性能进行了测定。实验结果表明：以硅丙乳液为成膜物质配制成的水性防火涂料理化性能优良，防火性能达到国家饰面型防火涂料一级标准。
关键词：水性；防火涂料；硅丙乳液
中图分类号：TQ630.7
文献标识码：A
文章编号：02534312(2010)050063~04
StudyofWaterborneFireproof Paint Lin Hongyan', Wang Chuncai?, Yang Hongwei?
(1.Daqing Petroleum Institute，Daqing,Heilongjiang 163318,China;
2. Daqing Longhua New Industrial Company, Daqing, Heilongjiang 163714, China)
Abstract: The mechanism of waterborne fireproof paint were introduced, Material selection and formula-tion optimization of fireproof system in development of intumescent silicone acrylic emulsion fireproof paint were described. The physical and chemical properties of the paint and the fireproof properties were deter-mined. Experimental results showed that the waterborne fireproof paint which composed of silicone acrylic emulsion has excellent physical and chemical properties. And it' s fireproof properties reach the first grade natronal standard of fireproof finish.
Key Words:waterborme;fireproof paint;silicone acrylic emulsion
0
引言
防火涂料是涂覆于可燃性基材表面，能降低被涂材料表面的可燃性，阻滞火灾的迅速蔓延，或是涂覆于结构材料表面，用于提高构件耐火极限的一类物质"。目前国内外高性能防火涂料均为水性乳液型膨胀防火涂料。水性膨胀型防火涂料的特点是：以水作分散介质、成本低、无毒、不污染环境、常温干燥，不仅具有防火性能，也有很好的装饰性能，涂层在常温下是普通涂膜，在火焰或高温作用下，可产生比原来涂层厚几十倍甚至上百倍的不易燃海绵状炭质层，起到有效阻止外部热源的作用，同时产生不燃性气体，如：CO，、NH，、HCI、HBr和水蒸气等降低可燃性气体的浓度和空气中氧的浓度，从面起到防火阻燃作用。水性膨胀型防水涂料主要由基料、脱水催化剂、炭化剂、发泡剂、额填料、分散剂、助剂等组成-2-3)
实验部分 1.1
实验仪器和原料
仪器：搅拌器、三辑研磨机、漆膜冲击器、柔韧性测试仪、作著介：林红署(1980一），女，研究生，讲师，从事化学工艺研究。
刮板细度计、附着力测试仪、酒精喷灯、涂-4"杯等。
原料：硅丙乳液、去离子水、聚磷酸铵、三聚氰胺、季戊四醇、二氧化钛、氧化锌、氨水、丙二醇苯醚、甲基硅油、六偏磷酸
钠溶液（10%）、羧甲基纤维素钠、其他助剂。 1.2制备方法
第一步：将六偏磷酸钠、羧甲基纤维素钠分别配制成10% 和2%的水溶液备用；
第二步：将要求量的去离子水加人烧杯中，开动搅拌器；第三步：低速搅拌下，将配方用量的脱水催化剂、炭化剂、
发泡剂、二氧化钛、分散剂、成膜助剂、助溶剂依次加人：
第四步：加人适量的消泡剂，然后高速搅拌（约 3000r/min），搅拌约20min；
第五步：用三辑研磨机将其研磨至要求细度；
第六步：为了不破坏乳液，将搅拌速降低度至800r/min，加人乳液及其他助剂，搅择约5min；
第七步：用稀氨水调节涂料pH至8左右：
第八步：用增稠剂羧甲基纤维素钠调节黏度至25~30s（涂~4"杯法）。
第九步：出料，检验。
63