应用研究
第42卷第6期 2012年6月
涂料工业
PAINT & COATINGS INDUSTRY
辐射型外墙隔热涂料的研制
彭红，杨
旗，陈明风，刘立军
（重庆建筑工程职业学院，重庆400039）
Vol.42No.6 Jun.2012
摘要：采用单掺、复掺试验方法，优化辐射型功能填料的量，获得辐射型外墙隔热涂料的最佳配方。绝对温升、半球发射率等性能测试表明，辐射型外增隔热涂料对建筑物吸收的热量具有一定的发射功能，可加快室内降温速率，从面达到良好的隔热降温效果，是一种主动降温型隔热涂料。
关键调：辐射型；功能填料；掺量：绝对温升；外墙隔热涂料
中图分类号：TQ637
文献标识码：A
文章编号：02534312(2012)06006004
DevelopmentofRadiantThermalInsulationExteriorCoating
Peng Hong, Yang Qi, Chen Mingfeng, Liu Lijun
(Chong Qing Vocational College Architectaral Engineering, Chongqing 400039, China)
Abstract: The best formulas of the radiant thermal insulation exterior coating was obtained by optimizing the radiate functional material through single doped or multi - doped process. The test results indicated that the radiant thermal insulation exterior coating could radiate the absorption heat of the buildings, which could speed up the cooling inside. Therefore the radiant thermal insulation exterior coating was a kind of ac-tive cooling type heat insulation coating and showed good heat insulation cooling effect.
Key Words: radiant ; functional material ; doped dosage; absolute temperature rise; exterior thermal insu-lation coating
辐射型外墙隔热涂料通过辐射的形式将建筑物吸收的日照光线和热量以一定的波长发射到室外，促使室内在日落后以室外同样的速率降温，从而达到良好的隔热降温效果，是种主动降温型隔热涂料")。
配制辐射型外墙隔热涂料的关键在于功能颜填料的选取，本研究对3类辑射性能优良的功能材料进行了掺量研究，并通过正交试验方法试配出一种辐射型外墙隔热涂料，并研究了其相关性能。
1
原料及设备
1.1主要原材料
纯丙烯酸乳液：金红石型二氧化钛：助剂；箱射型功能材料：800目、325目及纳米级的常温远红外陶瓷粉；3种金属氧化物（Mn0,AI,0,Fe,0,）;600目ZR-涂料粉。所有原材料均为市售。
1.2主要设备
FX1.5型高速搅拌分散机：J-1型电动搅拌器：QL-425 型超声波分散机：涂布器：表面热电偶：温度显示仪：红外灯等。
【基金项目】重庆市建设科技计划项目（域科字2010第【54】号）作者简介：影红（1983一），女，项士，主要从事化学建村等方西的研究。
60
1.3辐射型外墙隔热涂料的研制 1.3.1基础配方
辐射型外墙隔热涂料的基础配方如表1所示。
表1辐射型外墙隔热涂料基础配方
The basic formula of the radiate thermal insulation
Table1
coating
原材料
纯丙烯酸乳液二氧化钛
辐射型功能材料
助剂蒸馏水
1.3.2工艺流程
m/g 50 适量适量适量约50
（1）将分散剂加人蒸错水中，放至低速搅择机上充分搅拌均匀，将二氧化钛及功能材料按密度先小后大的顺序缓慢加人（转速约为3000z/min），同时根据情况加人适量消泡剂，然后缓慢加人成膜助剂及1/2增稠剂，低速搅拌均匀后再移