疏水支链水性聚氨酯的制备及性能研究
杨灿，姜京哲？
LONEPA Jul.2013
（1.华烁科技股份有限公司，武汉430074：2.武汉工程大学研究设计院，武汉430074）
摘要：以2-氨基-2-甲基-1,3-丙二醇与十八烷基异氰酸酯反应制备带支链的二元醇，再以支链二元醇、聚（已二酸-新戊二醇酯）二醇、二羟甲基丙酸与IPDI反应合成了具有疏水功能的支链水性聚氨酯。研究了支链二元醇用量等工艺参数对水性乳液粒径、耐水性、力学性能的影响，着重探讨了支链结构对不同基材粘接性能的影响。
关键调：梳型聚氨酯：乳液：异佛尔酮二异氰酸酯
中图分类号：TQ630.4*3
文献标识码：A
文章编号：0253-4312(2013)07-0001-05
PreparationandProperties ofWaterbornePolyurethane
with Hydrophobie Branched Chain
Yang Can'Jiang Jingzhe?
(1.HA/SOTechnologyCo.,Lad.,Wuhan430074,China;
2.Research and Design Institute of Wuhan Institute of Technology,Wuhan 430074,China)
Abstract:The diol with different branches was synthesized by the reaction of octadecyy! isocyanate with 2 - amino -2 -methyl -1,3 -propanediol, which was used to prepare the polyurethane emulsion with comb -branched chains (CPDs) with PAN,DMPA and IPDI The effects of branched diol dosage on emulsion particle size, water resistance and mechanical properties were discussed, focusing on the effect of the structure of branch chain on adhesion on different substrates.
Key Words:comb type polyurethane; emulsion; IPDI
内乳化法制备的水性聚氨酯具有较好的乳液稳定性和涂膜性能，但聚氨酯链上的亲水性基团易吸水，会导致湿环境下水性聚氨酯力学性能和粘接力下降，若通过减少乳化基团的用量来提高水性聚氨酯耐水性，又会导致乳液稳定性下降，故解决乳液稳定性和面水性的矛盾一直是水性聚氨酯研究领域的核心。目前关于提高水性聚氨酯耐水性的主要方法是在保持乳液稳定的情况下在水性聚氨酯链上引人疏水结构和交联结构[2-6],其中所引人的疏水结构主要有含氟链段和
含硅链段（7-
。但是含氟和硅的链段通常会显著降低
水性聚氨酯对基材的粘接性能.且价格昂贵，实用性不强。本研究以自制的含疏水烷基二醇和聚（已二酸新戊二醇酯）二醇为原料，制备疏水支化水性聚氨酯胶粘剂，研究了制备的工艺参数和支链二元醇用量对水性聚氨酯力学性能、粘接性和耐水性的影响
实验部分原料
1.1
十八烷基异氰酸酯：工业级，山东省平原永恒化
作者介：杨(1978一），男，工程师，主要从事高分子合成方面的研究