设计与试验DESIGNANDTEST 文章编号：1000-033X(2016)11-0046-04
沥青预裹覆碎石沥青用量研究张存公，李太杰，皇甫建红，石剑，冯红梅，李金哲
（西安达刚路面机械股份有限公司，陕西西安710119）
摘要：为了在封层施工中增大沥青与碎石的粘结面积与粘结牢度，提高封层质量，把沥青预衰覆碎石的相关试验及经验数据上升到理论计算层面，通过试验数据、理论计算相互参熙并引入“当量球”的方法，确定碎石预裹覆时沥青的用量等。研究结果表明，单粒径碑石在容器内的空间性质非
常接近球体在容器内的空间性质，单一粒径碎石的计算可以简化为按球体计算。关键词：同步封层；预衰覆碎石；当量球；沥青膜
中图分类号：U416.02
文献标志码：B
ResearchonAsphaltAmountforPrecoatingofGravel
ZHANG Cun-gong, LI Tai-jie, HUANGFU Jian-hong, SHI Jian, FENG Hong-mei, LI Jin-zhe
(Xi'an Dagang Road Machinery Co, , Ltd. , Xi'an 710119, Shaanxi, China)
Abstract: In order to improve the bonding capability between asphalt and gravel during the sealing construction and attain better quality, theoretical calculation was conducted on empirical data and related tests, based on which an equivalent sphere was introduced to determine the amount of asphalt for precoating the gravel. The results indicate that the spatial properties of gravel consisting of the same size of grain in the container are very close to those of the sphere, so the calculation can be simplified by considering it a sphere.
Key words: synchronous sealing; precoated gravel; equivalent sphere; asphalt film
0引言
随着中国公路交通的不断发展，沥青碎石同步封层施工工艺在各等级公路的新建和养护工程中被广泛应用")。在同一时间内酒（撒）布沥青和碎石，可以让两者具有较大的表面裹附强度，使沥青路面具有良好的防水性、防滑性、耐磨性和耐久性(2-4)。
封层所用碎石的形状为较复杂，多为不规则多面体颗粒，表面布满各种条纹、沟槽、凹坑与微孔。通过取芯对封层过的路面进行观察，发现一些碎石凸出的棱角部分与沥青有结合的痕迹，这是由于碎石表面粘有石粉，不利于沥青与碎石的粘合。当热沥青与碎石接触时，由于碎石的温度较低，热沥青表面的温度迅速下降，沥青的粘度增大，很难没润到碎石表面的条纹、沟槽、凹坑与微孔内与其粘合[5]。
通过增大沥青、碎石的粘结面积与粘结牢度（即增大沥青对碎石的表面裹附强度)是进一步提高沥
收稿日期：2016-04-16 46
万方数据
青路面路用性能的方法[6-9)。采用沥青预裹覆碎石进行封层施工可以克服以上缺陷，提高封层质量。
预裹覆碎石的沥青用量与碎石颗粒的表面积及沥青膜的厚度有直接关系。但是，由于封层用碎石的形状为较复杂，其表面积无法用常规方法计算。本文从球体在容器内的空间性质入手，进行单一粒径碎石在容器内的空间性质研究，找出切入点，引人“当量球”法来研究以前用常规方法不能计算碎石表面积的间题并作出结论，以备施工参考。
沥青预裹覆碎石
所谓沥青预裹覆碎石，即是将封层用碎石颗粒
表面预先没润粘结一层极薄沥青膜。在进行沥青碎右同步封层施工时，沥青与碎右的结合就变为沥青与沥青的结合，大大提高了沥青对碎石的裹附强度。因此，沥青碎石同步封层施工推荐优先选用沥青预妻覆碎石作为封层用材料。