应用分子筛干燥器降低130U002压缩机系统水含量
对显，，边清，范书胜，王发亮
（中国石油化工股份有限公司齐鲁分公司氟碱厂，山东淄博255411）
[关键调］二氯乙烷；精缩塔，压缩机；腐蚀;水含量；分子筛干燥器
[摘要］针对二氧乙烷精缩塔塔顶130U002压缩机系统因水含量高面造成的离蚀严重间题，增设了分子筛*，-01（68)-01(91)器
[中图分类号］TQ325.3；TQ051.21
［文献标志码］B
［文章编号］10097937(2012)04-0033-02
Applying a molcular sieve dryer to decrease the water content in 130U002 compressor system
LIUYu,BIANQing,FANShusheng,WANGFaliang
(Chlor-Alkali Plant, Qilu Branch Co., SINOPEC, Zibo 255411, China)
Key words; dichlorocthane; distillation tower; compressor; corrosion; water content; molccu-larsieve dryer
Abstract; To solve the scrious corrosion problem caused by high water content in 130U002 compressor system at the top of dichloroethane distillation tower, a molcular sieve dryer was added, and thus the water content was rcduced from 12 16 ppm to 8 9 ppm, so thc corrosion was signif-icantly slowed.
130U002是中国石油化工股份有限公司齐鲁分公司氟碱厂2*氧乙烯装置二氟乙烷精馏塔塔顶压缩机，是水分易富集的区域，系统物料呈弱酸性，不但易造成设备泄漏，面且腐蚀形成的氟化亚铁等盐类杂质积聚还会影响130U002压缩机及其密封泵的运行。本文中介绍了在130U002系统中增设填充物为胶体氧化铝的分子筛干燥器，有效降低了水含量，延长了装置的运行周期。
改造前的情况 1
130U002压缩机的作用有：①控制塔压，②将回收的乙烯增压送反应单元作为进料。
130U002是液环式压缩机，其循环液是压缩机出口深冷器冷凝下来的二氯乙烷液体，由于水分易富集，系统存在较严重的腐蚀，分离罐和出入口管线、出口冷却器等多次发生泄漏，不得不定期更换出口换热器，出口管线已经由碳钢改为衬里线；130U002压缩机出口分离罐一年内连续准漏3次，最短使用周期1个月，特别是腐蚀形成的氯化亚铁等盐类杂质积聚影响了
[收稿日期］201107-18
130U002压缩机及其密封泵的运行。130U002压缩机运行8年来检修15次，机泵机封更换4套，不但对精二氧乙烷纯度以及反应单元造成很大冲击，而且检修时尾气放空（乙烯放空量为0.5t/h），造成效益流失，污染环境，成为2*氯乙烯装置安全、稳定、优化运行的瓶颈。
2
改造过程
(1)原因分析。
二氧乙烷精馏塔塔项物料二氯乙烷本身呈弱酸
性，含水质量分数在10X10*°以下时，对设备管线基本上没有腐蚀；当含水质量分数在10×10-"以上时，随着水含量的增加，其腐蚀能力迅速增加。130U002系统所处的流程位置是水和酸性不凝气体易富集的区域，物料的酸度增加，对设备管线的腐蚀加剧，特别是装置内其他换热器一且泄漏，大量的水富集在130U002系统内，腐蚀设备管线，生成亚铁盐，这些亚铁盐又结合水分，并且附着在分离罐和换热器壳程内，亚铁盐内的结合水会不断释放，使130U002系统水含量长时间居高不下，导致设备严重腐蚀泄漏。
[作者简介］刘翌（1981一)，男，2004年毕业于大连交通大学化学工程与工艺专业，现就职于中国石油化工股份有
限公司齐鲁分公司氯碱厂氯乙烯车间。