第42卷第8期 2014年8月
聚氰乙烯 Polyvinyl Chloride
接枝共聚高抗冲PVC树脂的加工性能
石亮”，李成，黄传华
（四川金路树脂有限公司，四川德阳618500）
【关键调］PVC;接枝共案；冲击性能；加工应用
Vol.42,No.8 Aug-，2014
【摘要】将AIM增韧剂与普通PVC树脂、其他助剂共混制得了共混料；将AIM乳液与普适PVC树脂进行接枝共案制得了高抗冲PVC树脂，再与其他助剂共混制得了接枝料；比较了二者的抗冲改性效果。结果表明：接技料的抗冲改性效果更好。
【中图分类号】TQ325.3
【文献标志码］B
【文章编号】10097937(2014)08002703
Processing property of high impact PVC graft copolymer
SHI Liang,LI Cheng,HUANG Chuanhua
(Sichuan Jinlu Resin Co., Ltd., Deyang 618500, China)
Key words:PVC; graft copolymerization; impact property; processing and application
Abstract: Blend materials were prepared by blending toughening agent AIM, common PVC resins and other additives. High impact PVC resins were prepared by graft copolymerizing AIM emulsion and common PVC resins, then graft materials were prepared by blending the high impact PVC resins and oth-er additives. The impact properties of the two materials were compared. The results showed that the im-pact modification effect of graft materials was better.
PVC树脂应用广泛，截至2012年底，国内PVC 产能已经接近2400万a1]。PVC硬制品具有硬度大、阻燃、耐酸碱腐蚀、绝缘性能好且价格低廉等特点，所以被广泛应用于各个行业。但未经过增韧改性的PVC-U材料缺口冲击强度低、韧性差。因此，在PVC-U加工过程中通常须对其进行共混增韧改性处理，常用的增韧剂有：核壳结构的聚丙烯酸酯AIM;以丁苯共聚物为核，PMMA为壳层结构的共聚物MBS；含氟质量分数35%左右的氯化聚乙烯（CPE135系列）；丁苯橡胶相质量分数超过60% 的ABS高胶粉等(2)。但是共混增韧改性存在增韧剂分散不均匀、塑化困难、增韧剂用量大（如生产 PVC-M管材通常须共混6~8份AIM或者8~12 份MBS)等问题，且因为挤出时扭矩、熔体黏度大导致熔体流动性差，还须采用特殊螺杆结构的挤出机，无法使用现有挤出设备进行加工生产。
【收稿日期］】2014-02-17
目前主流的四大弹性体增韧剂中，CPE价格低廉，但是存在增韧改性效果差，制品耐热性差等缺点，比如要使PVC材料达到高抗冲级别时，CPE用量须增加到15~20份，此时材料的玻璃化转变温度仅65~70℃[3]。MBS和ABS高胶粉价格相对 CPE昂贵，且由于都含有大量的丁苯橡胶结构，其中残留大量双键，耐紫外线、耐氧化能力较差，因此不适于生产户外PVC-U制品。AIM由于其核层和壳层都是有较强耐候性的聚丙烯酸酯，故不存在 ABS和MBS的耐候性间题，应用范围相对较广。
笔者通过AIM乳液接枝共聚PVC树脂来增韧改性，并与共混增韧改性进行比较。
1试验部分 1.1主要原材料
PVC-SG5树脂，优等品，四川金路树脂有限公
【作者简介】石亮（1983一），男，助理工程师，2005年7月毕业于四川大学高分子科学与工程学院高分子材料专业，主
要从事特种树脂的研究开发。
27
万方数据