第41卷第7期
2013年7月【分析与测试】
聚氯乙烯
Polyvinyl Chloride
Vol.41,No.7 Jul.，2013
消光PVC专用树脂结构评价及测试方法的探索
徐珊梅·
（上海氟碱化工有限公司，上海200241）
[关键调］消光PVC；溶胶聚合度；凝胶含量；要胶体积润度；测试方法
[摘要］研究了测试方法、样品预处理和后处理、抽提时间和温度以及样品溶解和落胀条件对消光PVC树脂落胶案合度、凝胶含量以及疑胶体积影润度的影响，确定了消光PVC树脂溶胶象合度、凝胶含量、爱胶体积膨润度的测试方法。
[中图分类号］TQ325.3;TQ014［文献标志码］A［文章编号］10097937(2013)07-0034=05
ExplorationonmethodsforevaluatingandtestingthestructureofmattPvC specialresins
XUShanmei
(Shanghai Chlor-Alkali Chemical Co.,Ltd.,Shanghai 200241,China))
Key words: matt PVC; sol polymerization degree; gel content; gel volume swelling degree; test method
Abstract:Influences of testing method,sample prctreatment and post-treatment, extraction time and temperaturc as well as the sample dissolving and swelling conditions on thc sol polymeriza-tion degrec,gel content and gel volume swelling degrce of matt PVC resins were studicd.Methods of testing the sol polymcrization degrce, gel content and gel volume swelling degree of thc matt PVC resins were determincd
消光PVC专用树脂是由氯乙烯单体与交联剂共聚合成的含有适量凝胶的PVC树脂，采用这种新一代PVC树脂所加工的制品除了保持了PVC树脂原有的特性之外，还有消光性及较低的永久形变性。因此，消光PVC树脂扩大了PVC树脂的应用范围，具有广泛的市场前景。
在消光PVC树脂的合成过程中，选择合适的交联工艺是至关重要的，不仅交联剂的品种、用量直接影响消光树脂产品质量及其制品的消光效果，而且不同的工艺条件可以生产不同凝胶含量和凝胶体积膨润度的消光树脂1-37，因此选择合适的测试方法来准确表征消光PVC树脂的结构对聚合工艺条件的控制和加工成型都有一定的指导意义。
消光PVC树脂的结构用凝胶含量(G)、凝胶体积膨润度（Qv）、溶胶聚合度(P)3个参数来表征。目前，国内外对于这3个参数的测试方法没有统一的标准，一般都是根据各自产品的特点制定相应测试
［收稿日期］201305-20
方法。对于溶胶聚合度的测试，由于消光PVC树脂含有凝胶，因此不能简单地套用通用型PVC树脂的聚合度测试方法。据国外报道2，交联PVC树脂的凝胶含量采用抽提法测试，以四氢呋确为溶剂，用索格利特提取器进行48h回流来分离不溶于四氢呋南的物质，此不溶物为凝胶，聚合度以四氢味啸可着物(溶胶)根据JLS-K6721来测定。但此测试方法周期较长，不能适应科研项目进度的需求，而且由于回流时间过长、回流温度过高，可能使部分大分子错发生降解，最终导致聚合度偏低。
本文选用进口消光PVC树脂1*、进口消光 PVC树脂2*、国内某公司生产的消光PVC树脂（以下简称国产消光PVC树脂）、日本信越TK1000 通用PVC树脂作为测试样，比较了不同测试方法的测定结果，研究了样品预处理、样品量、抽提时间和温度、溶解溶胀条件对消光PVC树脂溶胶聚合度、凝胶含量以及凝胶体积膨润度的影响规律，确定了
[作者简介］徐珊梅（1966一)，女，工程师，毕业于华东理工大学，现就职于上海氯碱化工股份有限公司技术中心，从事
氯碱产品的分析测试及研究工作。 34