聚氢乙烯 Polyvinyl Chloride
涂壁剂喷嘴改造杨春革，，王承辉，沈国莲
（锦西工业学校，辽宁芦岛125001）
【关键调]聚氯乙烯；涂壁剂；喷嘴：改造
Vol.44.No.5 May，2016
【摘要］介绍了聚合签冷凝器涂壁剂的涂壁原理。指出由于原涂壁剂喷嘴结构存在弊端，致使喷射范围不理想，冷题器列管结垢严重：改成球形喷嘴后，不仅达到了预想的设计效果，而且提高了聚氧乙烯树脂的产量，降低了生产成本，取得了良好的经济效益。
[中围分类号】TQ325.3；TQ055.8
【文献标志码】B
[文章编号】10097937(2016)05004203
Modification of nozzles for wall coating agents YANG Chunping,WANG Chenghui, SHEN Guolian( Jinxi Technical School, Huludao 125001, China)
Key words: PVC; wall coating agent; nozzle; modification
Abstract: The coating principle of wall coating agents for condensers of polymerization reactors was in-troduced. It was indicated that the spray range was not ideal due to defects in the original structure of nozzles for wall coating agents, resulting in severe fouling on condenser tubes; after the nozzles were remoulded to spherical nozzles, not only were the expected design effects achieved, but also the production rate of PVC res-ins was improved, the production cost was reduced, and good economic benefits were achieved.
在聚氧乙烯生产过程中，聚合釜冷凝器安装在聚合釜顶部，在悬浮聚合反应中对釜内气体起到冷凝降温的作用，其运行好坏直接影响着聚合签内氟乙烯的聚合效果，甚至影响到与聚合釜相关联的浆料泵、压缩机等设备的正常运行。在生产过程中，聚合釜冷凝器最容易产生粘壁现象，不仅会影响冷凝器的传热系数、产品质量，而且还必须及时开盖检修清理，降低了运转率。方大锦化化工科技股份有限公司聚氯乙烯生产采用的是容积为105m”的聚合签，刚投产使用时，冷凝器列管内结垢额紫而且严重，从每次清理冷凝器结垢情况分析是喷嘴喷射范围不理想所致，因而决定改造冷凝器顶部涂壁剂喷嘴，由原来的直筒状改为球形。改造后涂壁剂喷嘴喷射压力、流量满足要求，喷射效果良好，涂壁剂涂
布均勾，PVC产量达到了设计能力。 1涂壁原理简介
涂壁剂是聚氯乙烯生产中必不可少的助剂之一，它是一种碱溶性高分子化合物，由于其内部分子结构中有OH一亲水基团，因此具有蔬油亲水功效。聚合
反应前，聚合釜冷凝器内要通人高温、高压水蒸气，涂壁剂常温下为液态，被蒸汽升温雾化后与其形成混合物进人冷凝器顶部，因冷凝器与聚合釜相通，进而进入聚合釜项部。此时聚合签底部搅拌器启动，搅拌聚合釜内气体形成反混气流，使涂壁剂均匀地附着在聚合釜内壁、搅拌挡板及冷凝器内壁上，形成一层薄薄的疏油亲水膜，从而完成聚合反应前的涂壁工作。由于涂壁剂具有疏油亲水作用，只允许悬浮体系中的水接近聚合釜及冷凝器内壁，排斥氯乙烯单体接近内壁，而单体引发剂在水中溶解度很小，水相中很少有引发剂、自由基和氯乙烯单体的存在，因此在水相中基本不发生聚合反应，即反应生成的自由基难以接触内壁，这样达
到了防止粘釜及粘冷凝器的目的。 2涂壁剂喷嘴改造情况介绍 2.1喷嘴改造前
聚合签冷凝器的内径为1524mm，圆筒状涂壁剂喷嘴内径为35mm，喷嘴中心线与冷凝器中心线相距300mm，喷嘴距列管距离为1905mm。冷凝器管程列管直径为（38.46±0.08）mm，长度为
【收稿日期】20160127
【作者简介】杨春草（1976一），女，高级工程师，高级讲师，2011年毕业于沈阳理工大学，机械专业工程硕士。