第44参第4期
2016年4月【分析与测试】
聚氟乙烯 Polyvinyl Chloride
提高PVC树脂热稳定性的分析与试验
崔增平“，王立华，贾晓庆，张金
（内蒙古君正能源化工股份有限公司，内蒙古乌海016000）
[关键调]PVC树脂；老化白度；热稳定性；热稳定时间；终止剂；液体锌
Vol.44,No.4 Apr.，2016
【摘要】分析了影响PVC树脂热稳定性的因素，试验研究了终止剂和热稳定剂对PVC树脂热稳定性的影响。试验结果表明：在聚合过程中添加液体锌热稳定剂对提高PVC树脂的热稳定性有显著效果。
[中图分类号］TQ325.3;TQ014【文献标志码】B【文章编号】10097937(2016)04-0023-04
Analysis and experiment on improving thermal stability of PVC resins
CUI Zengping,WANG Lihua,JIA Xiaoqing,ZHANG Jin
(Inner Mongolia Junzheng Chemical Industry Co., Ltd.,Wuhai 016000, China)
Key words: PVC resin; aging whiteness; thermal stability; thermal stability time; terminating agent; liquid zinc
Abstract: Factors of influencing the thermal stability of PVC resins were analyzed. Experiments were conducted to study the effects of teminating agents and thermal stability agents on thermal stability of PVC resins. Experiment results showed that the addition of liquid zinc heat stabilizer during polymeriza-tion had a significant effect on improving the thermal stability of PVC resins.
PVC树脂是五大通用塑料之一，因价格低廉、性能优异而得到了广泛的应用。近年来，随着下游加工行业的不断发展以及市场竞争的日益激烈，加工企业对PVC树脂的热稳定性越来越关注，并提出了更高的要求。
内蒙古君正能源化工股份有限公司（以下简称君正化工)32万VaPVC项目于2013年9月投产。该项目聚合装置引进了法国阿科玛公司技术，采用 143m"聚合釜，属于目前国内最大的釜型，主要生产SG5型PVC树脂。2014年转入正式生产后，经过不断调整，PVC树脂各项性能均达到国家标准优等品的要求，但下游用户经常反映PVC树脂的热稳定性较差，而且波动较大。为了更好地改善PVC树脂品质，提高PVC树脂的加工性能，满足客户的使用要求，笔者对提高PVC树脂热稳定性的措施进行了分析与试验。
【收稿日期】2015-0202
1PVC树脂热稳定性的衡量指标
PVC树脂在加工过程中存在着热降解的缺点，它的加工温度（160℃以上）比分解温度（120~130 C)还高，因此要将PVC树脂变成制品，就必须在加工成型过程中添加热稳定剂，以延缓或阻止PVC树脂的热降解。若PVC树脂本身的热稳定性差，下游加工企业须增加热稳定剂的用量；若PVC树脂的热稳定时间波动较大，会给加工企业带来加工配方调整频繁的问题。目前，国家标准对PVC树脂的热稳定性没有具体的指标要求，下游企业普遍采用的衡量指标为热稳定时间。据了解，PVC树脂加工行业内目前普遍反映PVC树脂的热稳定时间（温度180 ℃)控制在4min以上为最好，低于3min就可能会影响到制品的加工。
【作者简介】崔增平（1974一），男，工程师，现任内蒙古君正能源化工股份有限公司生产副总经理。
23
万方数据