第38第9期 2010年9月
聚氯乙烯
Polyvinyl Chloride
高性能冰箱门封条用PVC粒料的制备
夏振华·
（安徽省化工研究院，安徽合肥230041)
[关键词】PVC;冰箱；门封条；粒料
Vol.38，No.9 Sep.，2010
摘要］针对抗迁移性和硬度变化率，对冰箱门封条用PVC粒料配方进行了优化。试验确定的参考配方为： PVC100份，TOTM20份，ESO2份，DOS6份，钙锌复合稳定剂4份，重质碳酸钙44份，硬脂酸0.4份，石蜡0.3 份，其他助剂适量。该PVC粒料各项性能均达标，且成本变化不大。
[中图分类号】TQ325.3
［文献标志码］B
［文章编号】10097937(2010)09002803
Preparation of PVC granulars for refrigerator door sealerwithhigh performance
XIAZhenhua
(Anhui Research Institute of Chemical Industry, Hefei 230041, China)
Key words: PVC, refrigerator; door sealer; granular
Abstract: According to migration resistance and changing rate of hardness, the formula of PVC granulars for refrigerator door sealer is optimized. The reference formula obtained by experiments isPVC100，TOTM20，ESO2，DOS6，Ca/Zncomplexstabilizer4，hcavycalciumcarbonate44， stcaric acid .4 and paraffin wax 0.3parts,and some other additives.Each performance of this PVC granulars is appropriate to the standard with little changes in production cost.
随着人们对健康的关注以及冰箱行业的发展，人们对冰箱配件的要求越来越高。冰箱门封条除要求力学性能、抗迁移性合格外，还要求对人体无毒，满足REACH和RoHS的要求。
以前开发的无毒冰箱门封条在抗迁移性和硬度
变化率方面不能兼顾，一项能满足要求，另一项就不能达标。因此，笔者重点研究了冰箱门封条这2项性能的平衡，开发了高性能冰箱门封条用PVC粒料。
1配方研究 1.1原料的选则 1.1.1PVC
为达到拉伸强度和断裂伸长率的要求，并充分考虑成本因素，笔者选用了上海氯碱化工股份有限
，［收稿日期］2010-06-02
公司的PVC-SG3型优级品树脂。 1.1.2增塑剂
为达到REACH、RoHS和抗迁移性的要求，应选用环保增塑剂。环保增塑剂有DOTP、ESO、DOS 等，既环保又具有抗迁移性的增塑剂有TOTM、聚酯类增塑剂等。
影响抗迁移性的主要因素是增塑剂，次要因素是钙锌稳定剂和内外润滑剂。这些物质在高温下都会在HIPS板上析出并沉积。为了满足迁移量≤30 mg的要求，必须选取具有抗迁移性的增塑剂。考虑成本因素，笔者选取了TOTM为主增塑剂，ESO DOS为辅助增塑剂。同时配合调整热稳定剂和润滑剂的用量，以满足抗迁移性指标要求。
为了达到硬度变化率的要求，需仔细调整增塑
【作者简介夏振华(1965一)，男，安徽省东至县人，高级工程师，1988年7月华业于断江大学化工系高分子化工专业，主要从事高分子材料的合成和加工研究工作，完成了人造毛皮用丙烯酸酯乳液防风胶、建筑用PVC/CPE防水卷材、抗静电粉
末涂料、高速卷钢粉末涂料等多项课题，发表论文20多第。 28