第41卷第5期 2013年5月
聚氯乙烯
Polyvinyl Chloride
超低聚合度PC树脂生产技术的研究
石亮“，黄传华
（四川金路树脂有限公司，四川德阳618500）
关键词］PVC;超低聚合度；聚合工艺；应用
Vol.41, No.5 May,2013
[摘要］概述了国内超低聚合度PVC树脂生产工艺的研究进展以及应用情况，介绍了超低聚合度PVC树脂树脂的熔体流变性能和作为SG8型PVC树脂聚合物型增塑剂使用时的增塑效果。
[中图分类号］TQ325.3
[文献标志码］B
3［文章编号］1009—7937(2013)05—0012—04
Research on theproduction technology of PvC resins withultralowpolymerization degree
SHILiang,HUANGChuanhua
(Sichuan Jinlu Resin Co ., Ltd ., Deyang 618500, China)
Key words : PVC; ultralow polymerization degree ; polymerization process ; application
Abstract : The research progress on domestic production technology and application situations of PvC resins with ultralow polymerization degree are summarized . The development progress of PvC resins with ultralow polymerization degree is introduced . The relationship between chain-ex-tender mercaptoethanol amount and average polymerization degree gelation temperature is discussed emphatically . The rheological properties of PvC resins melt with ultralow polymerization degree and their plasticizing effect on SG8 PVC resins are tested.
超低聚合度PVC树脂指聚合度低于600的疏松型PVC树脂，其平均聚合度最低可以达到300。该类型树脂具有表观密度高、凝胶化温度低、塑化时间短、熔体流动性好等特点，在加工过程中熔融塑化速度快，熔体黏度小，加工温度低，熔融因数高，因此具有很广阔的用途。
超低聚合度PVC树脂的研究进展
目前，国外PVC生产企业已经将超低聚合度
PVC树脂工业化，国内也有部分PVC生产企业进行了超低聚合度PVC树脂的小试和中试。其中，谢雷用10L聚合釜制得了平均聚合度600、K值55 的超低聚合度PVC糊树脂。刘松涛2}对分散体系、亏发体系及链转移剂的用量进行了优化，用悬浮法
*［收稿日期］2013—0308
小试制得了平均聚合度500～600的PVC树脂。杨卫国3通过试验考察了链转移剂用量与PVC聚合度之间的关系。文献「4公布了一种平均聚合度 400的超低聚合度PVC树脂的生产方法。张利明5通过试验制得了平均聚合度400的超低聚合度 PVC树脂,并且探讨了巯基乙醇加料方式对树脂颗粒形态的影响。王国文对两种链转移剂的效果进行了评估。文献7公布了一种新型溴代烷链转移剂在超低聚合度PVC树脂生产领域的应用方法。张京友等研究了平均聚合度500的超低聚合度 PVC树脂的聚合工艺,并进行了加工配方及力学性能的评价。詹晓力等系统地研究了链转移剂蔬基乙醇对悬浮法PVC树脂颗粒形态的影响认为筑基
[作者简介］石亮（1983一），男，助理工程师，2005年毕业于四川大学高分子科学与工程学院高分子材料专业，主要从
事特种树脂研究开发工作。 12