第44卷第12期 2016年12月
聚氯乙烯 Polyvinyl Chloride
Vol.44, No.12 Dec.,2016
高聚合度PVC树脂的将性及其在电线电缆中的应用
罗文龙，苑会林
（北京化工大学材料科学与工程学院成型加工实验室，北京100029）
【关键调】高聚合度PVC；性能；电线；电缆
【摘要】采用不同案合度PVC作为基体，研究了高聚合度PVC对制品的玻璃化转变温度、力学性能、加工性能的影响。结果表明：高聚合度PVC能够有效地提高断裂伸长率、拉伸强度、玻璃化转变温度、增塑剂吸收能力、加工温度，在耐热等级高的电线电缆中有着广泛的应用。
【中图分类号】TQ325.3
【文献标志码】B
【文章编号】1009 7937(2016)12-003004
Properties of high-polymerization degree PVC resins and
their applications in wires and cables
LUOWenlong,YUANHuilin
(College of Material Sci. and Eng. , Bejing University of Chemical Technology, Beijing 100029, China)
Key words: high-polymerization degree PVC; performance; wire; cable
Abstract : The influence of high-polymerization degree PVC used as matrix on the mechanical prop-erties, glass transition temperature and processing performance of products was studied.The results showed that high-polymerization degree PVC could effectively improve the properties of products, such as elongation at break, tensile strength, glass transition temperature, plasticizer absorption ability，, and processing temperature, and it would be widely used in wires and cables of high heat resistance grade.
通用型PVC树脂的聚合度在600~1500之间。高聚合度PVC(HPVC）树脂一般是指平均聚合度在1700以上或其分子间具有轻微交联结构的 PVC树脂，其中以案合度为2500的HPVC最为常见，现在可以生产或可以市场化的HPVC树脂有聚合度3000的和聚合度4000的。与普通PVC相比， HPVC分子质量高，分子链长且卷曲性大，分子链间的缩结点增多，从而使HPVC分子链间的作用力增强，分子链间的滑移困难。因此，HPVC可提供高的力学性能和耐热性能。同时，又由于HPVC能吸收较多的增塑剂，故其软制品不仅强度高、耐热性好，而且回弹性好、压缩永久形变也小，耐磨、耐寒性优异，具有热塑性弹性体的特点(1)。人们对于HPVC 与其他聚合物共混做了很多研究(2-})，笔者主要研
【收稿日期】2016-0330
究HPVC树脂的特性及其在电线电缆中的应用。 1试验
1.1主要原材料
PVCS-2500、S-1000S-650，中国石油化工股份有限公司齐鲁分公司；DOP，山东辰宇化工有限公司；TOTM，济南格瑞化工有限公司：三盐基硫酸盐，新乡市科峰化工有限责任公司；二盐基硫酸盐，上海之臻化工有限公司；聚乙烯蜡，上海和氏壁化工有限公司；硬脂酸铅，石家庄市德塑助剂有限公司；碳酸钙，南京恒峰碳酸钙厂；硬钙，石家庄佳拓化工科技有限公司；硼酸锌，山东秀诚化工有限公司；三氧化二锑，广州利弘基化工有限公司；炭黑，天津