聚氯乙烯 Polyvinyl Chloride
氟乙烯-丙烯酸丁酯共聚树脂的工业化生产
黄东，宋晓玲，贺盛喜，沈姗姗
（新疆石河子中发化工有限责任公司，新幢石河子832000）
[关键调］氯乙烯；丙婚酸丁酯；共案树脂：工业化生产
Vol.40, No.4 Apr.，2012
[摘要］在7m”聚合签中采用悬浮聚合工艺工业化生产了氯乙烯-丙婚酸丁酯共案树脂，在小试配方基础上调整了分散剂的配比和用量，采用在线实时示踪剂色谱联动控制法控制丙烯酸丁酯的加人速度，并采用了案合中途注水工艺及改进的防粘签工艺。工业化产品符合企业标准要求，可在PVC型材生产中替代ACR使用。
[中图分类号］TQ325.3
［文献标志码］B［文章编号］1009-7937(2012)04-000904
Industrial production of vinyl chloide-butyl acrylate copolymer resins
HUANGDong,SONGXiaoling,HEShengri,SHENShanshan
(Xinjiang Shihezi Zhongfa Chemical Industry Co., Ltd., Shihezi 832000, China) Key words: vinyl chloride; butyl acrylatc; copolymer resin; industrialization production
Abstract: Vinyl chloide-butyl acrylate copolymer resins were produced by suspension polymer-ization in an industral 7 m’ polymcrization rcactor. On the basis of small-scale formulas, thc ratios and dosages of dispersants were adjusted, the addtion rate of butyl acrylate was controlled by onlinc rcal-timc traccr and gas chromatography, and process of injccting watcr during polymcrization and improved antiscaling process were adopted. The industrial products obtained conformed to the en-terprisc standard, and could be applied to thc production of PVC profiles as substitutes for ACR
氯乙烯一丙烯酸酯共聚树脂是一种综合性能良好的共聚树脂，其性能大大好于氟乙烯一醋酸乙烯等共聚树脂，最早由德国IG法本公司开发成功。20世纪60 年代，欧洲、日本开始生产该树脂。经过几十年的发展，氯乙烯一丙烯酸酯共聚树脂可采用悬浮聚合法、乳孔液聚合法、微悬浮聚合法生产，可以根据树脂的用途选用不同的方法生产，以满足用户的需求。近年来，由于全球丙烯酸酯的产量和品种不断增多，生产规模不断扩大，生产技术水平不断提高，其价格不断降低，使氧乙烯一丙烯酸酯共案树脂的成本降低，市场不断扩大"。用丙烯酸酯改性的氯乙烯共聚物是良好的电子、电器注塑专用料，可提高制品的冲击强度和加工流动性；用该树脂生产的硬质注塑件表面光滑，没有症点，产品质量完全符合技术要求[2]。
新疆石河子中发化工有限资任公司（以下简称新疆中发公司)根据市场的需求，开发出了氯乙烯一丙烯酸丁酯共聚树脂，经过20L小釜聚合试验后，
，［收稿日期］2011-1109 万方数据
在7m"聚合釜上进行了工业化试生产，生产的氯乙烯-丙烯酸酯共聚树脂质量符合企业标准，化学组分均匀，塑化性能和力学性能良好。
1原材料及设备 1.1原材料
氯乙烯：聚合级，新疆中发公司；丙烯酸丁酯：中
国石油兰州石化公司；聚乙烯醇：日本合成化学公司；羟丙基甲基纤维素：山东瑞泰化工(集团)有限公司；过氧化二碳酸二乙基已酯、过氧化新酸异丙苯酯：山东淄博助剂厂；碳酸氢铵：乌鲁木齐氮肥厂；硫醇甲基镐热稳定剂：北京上北化工有限责任公司；液体锌：武汉开元化工有限责任公司；终止剂：天津现代科技化工助剂厂pH值调节剂：NaOH水溶液；颗粒调节剂：KFB-002，新疆中发公司;去离子水、防粘釜剂：新疆中发公司。