力化学改性对PVC/滑石粉复合材料
耐热性能及力学性能的影响
陈光顺"，邓志伟，郭少云"”，李光宪
（四川大学高分子材料工程国家重点实验室，四川成都610065）
【关键调】PVC;滑石粉；力化学；力学性能；耐热性能
Vol.42, No.6 Jun.，2014
[摘要】考察了不同滑石粉用量下，力化学改性对PVC/滑石粉复合材料耐热性能和力学性能的影响。结果表明：力化学改性不仅可以提高PVC/滑石粉复合材料的耐热性能，还能改善其力学性能，是一种简单、有效的改性工艺。
【中函分类号】TQ325.3
【文献标志码】B
[文章编号】10097937(2014)06001704
Effectsofmechanochemicalmodificationon
heatresistanceandmechanicalpropertiesofPvC/talccomposites
CHENGuangshun，DENGZhiwei，GUOShaoyun，LIGuangxian
(State Key Laboratory of Polymer Materials Engineering of Sichuan University,Chengdu 610065, China)
Key words; PVC; talc; mechanochemistry; mechanical property; heat resistance
Abstract: The effects of mechanochemical modification on the heat resistance and mechanical prop-erties of PVC/talc composites with different amount of talc were investigated.The results showed that mechanochemical modification could not only improve the heat resistance of PVC/talc composites, but also improve the mechanical properties. This was a simple, effective modification process
Foundation item: Key Project of National Natural Science Foundation of China(51133005)
作为五大通用塑料之一的PVC被广泛应用于化学建材，其中包括大量的PVC门窗。近年来，出于节能的需要，建筑中常常要求采用节能门窗。 2011年3月1日颁布实施的有色金属行业标准YS/ T729一2010《铝塑复合型材》，规定了PVC合金用于节能窗的相关标准。但PVC分子本身的结构特点决定了其不像工程塑料那样具有较高的维卡软化温度和较低的线性热胀系数，通常PVC材料的维卡软化温度仅在80℃左右，而线性热胀系数达 6.88×10-5℃1,因此常常需要对PVC进行共混改性以提高其维卡软化温度并降低其线性热膨胀系
【收稿日期】2014-04-03
【基金项目】国家自然科学基金重点项目（51133005）
数，达到在节能窗的长期使用过程中的性能及安全要求(1-4)。
笔者考察了力化学改性工艺对PVC/滑石粉复合材料（以下简称复合材料）耐热性能和力学性能的影响，试图在保持复合材料力学性能的前提下，找到一种简单、有效的方法来提高复合材料的热性能。 1试验部分