疏水涂层的制备及性能
雷辉卢鹉
郭家胜
李颖
曾一兵
（航天材料及工艺研究所，北京100076）
文摘涂层的疏水效果不仅取决于涂料自身表面自由能的大小，还与其表面粗糙度有密切的关系。通过向涂料中添加疏水助剂降低表面能，控制喷涂工艺提高涂层表面粗糖度，制备了疏水涂层。研究了疏水剂的种类、用量以及表面粮度对涂层疏水性能的影响。结果表明：当疏水剂的用量为5wt%，表面略微粗楚时，接触角达到139°，具有良好的疏水效果。
关键词疏水剂，表面自由能，表面报疑度，接触角
Preparation and Properties of Hydrophobic Coating
Lei Hui
LaWu
Guo Jiasheng
Zeng Yibing
LiYing
( Aeroepace Reaearch Institute of Materials & Processing Technalogy,Beijing100076)
AbstractHydrophobic effect of coating depends not only on its own surface energy, but also the surface rough-ness, The hydrophobic coating was prepared by adding hydrophobic additives to the coating to reduce the surface ener-gy, and controlling spraying process to improve the surface mughness. The effects of types and amounts of hydropho-bic additive and surface roughness to hydrophobic property of couting were studied. The results show that the contact angle can reach 139° with good hydrophobic effect when the amount of hydrophobic additive is 5% , and the coating has slightly rough surface.
Key wordsHydrophobic additives,Surface energy,Surface roughness,Contact angle
0引言
疏水涂层具有独特的表面性能，如自洁性，防污性，疏水性等，并在水下航行器减阻等众多领城具有重要的应用价值1-3]。近些年来，具有超疏水性的界面材料引起了人们的广泛关注，研究者通过多种方法来制备超疏水表面，其中在低表面能材料的表面构筑粗糙表面是获得超疏水性能的有效途径[4-9]。Feng 等人[101利用冷喷涂技术，在具有丝网结构的不锈钢表面上制备均勾的聚四氟乙烯涂层，获得超疏水表面，但需要在基材表面预先构筑微结构。Wang等人(11}在案苯乙烯涂层中添加Si,微粒，增加了聚苯乙烯涂层的表面粗糙度，提高了其疏水性。但由于现有超蔬水技术大多工艺复杂，无法在常温条件下大面积制备出超疏水涂层表面，同时所制备的超疏水表面力学性能较差，极大地制约了其在实际生产中的应用。
本文优选了丙烯酸树脂基体和功能颜料、填料，收稿日期：201102-16
通过向涂料中添加疏水剂和控制涂层的喷涂工艺技术，制备了疏水涂层，研究了涂料配方和喷涂工艺对
涂层疏水性能的影响规律。 1实验
1.1原材料
丙烯酸树脂，江苏三木公司；猷青蓝，市售：白炭黑，沈阳化工股份有限责任公司；润土，天津华联有机陶土化工福利厂；钛白粉，杜邦公司；导电粉、疏水剂，市售。
1.2试样制备
将一定量的树脂、各种颜填料按比例混合后加人适量疏水剂及其他助剂，揽拌均匀后放入球磨瓶中球磨6~8h后得到涂料，将涂料过滤后加入固化剂，通过控制涂料的喷涂工艺在马口铁、铝合金试板上制备
蔬水涂层，于室温下干燥固化。 1.3性能
涂层的接触角采用上海中晨数字技术设备有限
作者简介：雷辉，1984年出生，项士，主要从事功能涂料的研制与开发。E-mail:jlbclh@sins.c0
字航材料工艺htp://www.yhelgy.com2011年第5期
9 —