芯子宽厚比对铝蜂窝夹层结构平压强度的影响
章妮卢克非
崔文龙
（航天材料及工艺研究所，北京100076)
文摘用正六边形代替实际蜂芯，推导了夹层结构的平压强度与芯子宽厚比的关系，并对八种规格的芯子平压强度进行统计，统计结果虽然与推导的结果有偏差，但规律却是一致的，即蜂窝夹层结构的平压强度随着芯子宽厚比d/t,增大呈负指数减小。
关键调铝烽窝，夹层结构，宽厚比，平压强度
中图分类号：V45
D0I;10.3969/j. issn.10072330.2016.02.008
EffectionofRatioof WidthtoThicknessofAluminumHoneycomb
SandwichStructureofFlatwiseCompressionStress
ZHANGNi
iCUIWenlong
LUKefei
(Aerospace Research Institute of Materials & Processing Technology,Beijing100076)
AbstractUsing the hexagon instead of the actual honeycomb core, the flat compression strength of sandwich structure and its relationship with the width to thickness ratio was deduced. Eight kinds of specifications of core flat compressive strength were evaluated. Statistical results revealed that although there are deviations from the deduced results, the law is consistent, namely honeycomb sandwich structure of flat compression strength decreases exponen-tially with the increase of core width to thickness ratio d/t,.
Key wordsAluminum honeycomb,Sandwich structure, Ratio of width to thickness,Flatwise compression stress
0引言
夹层结构在复合材料领域是一种常见的结构，通常由蒙皮和芯体组成，具有比强度、比模量高，密度低和透波性好等特点。在航空、航天、船舶、建筑、桥等领域广泛应用，尤其在航空和航天领域应用最为广泛，如大型运载火箭整流罩、仪器舱、卫星支架、贮箱共底，卫星的电气结构板、天线反射器、太阳能电池阵基板，载人返回舱侧壁、防热大底以及天线罩等[1]。
夹层结构芯子包括泡沫、蜂窝和软木等轻型材料。由于夹层结构的组成复杂，蒙皮材料的强度和模量高于芯材，为反映夹层结构的真实性能，其试验方法较为复杂(2]，而平压试验方法是其中较为简单的方法。夹层结构或芯子的平压强度是通过在垂直于芯材平面（即厚度方向）施加压缩载荷，直至材料发生破坏或届服，计算单位面积上的压缩载荷(3)（图 1），可见，对于夹层结构，芯子是主要的承力部位，芯子的平压强度决定了夹层结构的平压强度。芯子的
收稿日期：2015-1102
平压强度与芯子材料类型、形状规格和芯子密度等都有密切关系【4]。
上压板夹层结构下压板
图1平压强度测试示意图 Fig. 1Schematic diagram of flatwise
compression Strength tset
对蜂窝等格子芯材，承受载荷的是蜂窝芯壁，蜂窝芯壁由单层壁和双层壁构成，这种构成及芯子边长与蜂壁厚度的比（宽厚比），构成了蜂窝芯子的基本结构特征。本文对八种芯子规格的蜂窝芯子测试数
作者简介：章妮，1983年出生，硕士，主要从事材料力学性能测试研究。E-mail；56479491@qq-con