·工程实践·
肖军
一种防热涂层的应用工艺
章凯军？
李晓升!
曾一兵3
（1中国空空导弹研究院，洛阳471009）（2北京机电工程总体设计部，北京100854）（3航天材料及工艺研究所，北京100076）
李晨光3
文摘防热涂层对小型高速战术导弹结构实现先进设计和防热性能十分重要，而应用工艺直接关系到其防热效能。本文通过对表面处理、底层涂料、填料分散、喷涂干燥等工艺的研究，使防热涂层附着力、防热性能以及环境适应性均满足使用要求，最终确定了一种可靠的施工工艺方案。
关键词热防护，材料与工艺，涂层，试验
AnAppliedTechnologyforThermalProtectionCoating
Xiao Jun
Zhang Kaijun?
Li Xiaosheng'
Zeng Yibing
(1 China Airbome Missile Academy,Luoyang 471009)
Li Chenguang
(2 Beijing System Design Institute of Electro-Mechenic Engineering,Bejing 100854)(3Aerospace Research Institute Materials & Processing Technology,Bejing 100076)
AbstractThermal protection coating is very important for small ultra-high speed tactical missile to achieve ad-vanced design and excellent performance.Felicitous material & technology is a key to realize it for execution of the coating. In this paper,surface treatnments, primers,fller decentralization and spraying technology is studied, and then tests are performed. Test result show that perfomance of coating, as adhesive force, thermal protective perform-ance and environment adaptability,meet the requirements. An effective process scheme is developed.
Key wordsThermal protection, Materials & technology, Coating, Tests
0引言
利用外防热涂层改变弹体表面热物理特性，保障高速战术导弹在弹道飞行中不因气动过热导致结构灾难性故障；避免弹体内部仪器仪表不因温度过高出现故障是结构设计的重要工作，而涂层防热效果和质量与实施过程的材料与工艺控制直接相关。采用镁或铝合金、钛合金、高强钢，可获得更远的射程和机动性，然而表面涂层对钛合金等材料的附着力较低，需要进行表面处理以提高涂层与基体的结合力。铝合金阳极氧化、钢铁发蓝发黑、钛合金吹砂或阳极氧化
收稿日期：2013-08-13
基金项目：航空基金2010ZD12009
处理可以显著提高涂层的结合力。
实践发现，导致弹体表面防热涂层附着力显著下降更显著的因素并非表面处理后放置时间长，而是活化表面暴露于大气中受到污染导致涂层在温度骤变中出现脱粘、开裂等问题；如某钛合金壳体在低温/高温的循环中出现批次性脱粘、开裂故障。本文讨论了外用热防护涂层施工过程有关的表面处理、底层涂料、填料分散、喷涂干燥条件以及防热和环境试验有
关应用研究，为相关应用提供借鉴。 1试验
作者菌介：肖军，1962年出生，工学博士，高级工程师，主要从事航空航天结构兼容与热防护设计工作。E-mail：qianqianhui@163.com