ISSN10003762 CN41 1148/TH
轴承2017年1期 Bearing 2017, No. 1
32 34
D0I: 10. 19533/j. issn1000 3762. 2017. 01. 009
锻造成形方式对外圈滚道周向非相关磁痕的影响
张玲",2，杨争1,2，陈学武，陈治山12，刘首1,2
(1.洛阳LYC轴承有限公司，河南洛阳471039;2.航空精密轴承国家重点实验室，河南阳471039）摘要：锻造成形的圆柱轴承外圈经过车加工、热处理、磨加工后经磁粉探伤检验发现其滚道面出现周向非相关磁痕。对自由锻和压力机2种锻造成形方式进行对比试验，结果表明，自由锻成形方式是减少滚道周向非相关磁痕最佳锻造方式。
关键词：滚动轴承；锻造成形；流线；滚道；周向非相关磁痕
中图分类号：TH133.33;TF124.38
文献标志码：B
文章编号：10003762(2017)01003203
InfluenceofForgingFormingMethodsonCircumferentialNon-
Relevant Magnetic Marks on Outer Ring Raceway Zhang Ling"., Yang Zheng'2, Chen Xuewu', Chen Zhishan'2, Liu Jing.2
( 1. Luoyang LYC Bearing Co. , Lid. ,Luoyang 471039, China;2. State Key Laboratory of Aviation Precision Bearings,
Luoyang 471039, China)
Abstract : The magnetic particle test shows that there are circumferential non relevant magnetic marks on raceway sur face of forged and fomed outer rings of cylindrical roller bearings after turning, heat treatment and grinding. The com parative test is carried out for two kinds of forging forming methods. The results show that the free forging forming meth-od is best forging method for reduction of circumferential non relevant magnetic marks on raceway.
Key words : rolling bearing forging forming ; streamline;raceway ;circumferential non relevant magnetic mark
轴承套圈在磁粉探伤过程中，虽然非相关磁痕相对于相关磁痕的发生率很低，但也时有发生。非相关磁痕不是来源于真正的缺陷，但用户在验收时极为严格。在大型圆柱滚子轴承的制造过程中，外圈锻造成形方式对滚道周向非相关磁痕的产生影响较大。大型轴承外圈常见的锻造成形方式有1t锤自由锻和1000t压力机。自由锻锻造成形时，采用缓慢的变形速度和较小的变形力，具有灵活性、适应性强的特点，可以更好地满足用户要求；压力机锻造成形由于生产效率高，也逐渐被推广使用。当外圈使用压力机成形时，磁粉探伤发现其滚道部位常存在大面积、均沿圆周方向分布的多条短线状磁痕，针对样圈进行了多次分析及相关工艺试验，证明不同锻造方式对此类批量磁痕的产生有影响，为此，进一步开展了相关锻造工艺试验，并加以验证。
收稿日期：2016-03-01；修回日期：2016-06-17 万方数据
试验 1
1.1试样材料及状态
试样材料采用GCrl8Mo电渣重熔钢，共进行两批次试验，每次试验均选择钢厂提供的同一母炉号的原材料组批。材料进厂检验其化学成分及非金属夹杂等项目均符合TB/T3010—2001&铁道车辆滚动轴承高碳络轴承钢订货技术条件》要求。材料状态为热轧退火态，棒料直径为110mm。该批原材料采用多台阶塔形试样进行荧光探伤"
无带状碳化物磁痕，均符合企业标准。 1.2锻造工艺及成形设备
外圈外径为250mm，其锻造工艺流程：下料 →中频感应加热→锻造成形（锻粗→冲孔→扩孔 →整径)一→正火→退火。分别采用1t锤自由锻生产线（简称自由锻)和1000t压力机生产线（简称压力机)进行锻造成形。