doi:10.3969/j.issn.16715152.2014.03.005
豆利军等·聚乙炜燃气管材对接焊焊口麻点研究
聚乙烯燃气管材对接焊焊口麻点研究
口四川亚大塑料制品有限公司（611830）豆利军刘松林
摘要：由于聚乙烯燃气管材存放环境因素的影响，在实施对接焊时，在对接焊焊口处可能会出现麻点
现象，严重的会影响运行管线的安全。本文简要介绍了对接焊焊口麻点形成的原因，开展了不同材料聚乙烯燃气管材对接焊焊口麻点试验，研究了不同材料管材的吸水性能以及水分含量对不同材料管材对接焊焊口质量的影响程度，并进行了采用热烘法减少聚乙烯对接焊焊口麻点的试验研究，找出了简单有效的减少焊口麻点的方法。
关键词：聚乙烯燃气管材热熔对接焊焊口麻点热烘法
PolyethyleneGasPipeButtWeldingWeldPittingResearch
Sichuan Chinaust Plastics Product Co,Lid. Dou Lijun Liu Songlin
Abstract : Since polyethylene gas pipe storage environmental factors in the implementation of butt welding, butt welding
weld in place pitting phenomenon may occur, seriously affect the operation of pipeline safety. This paper introduces the butt weld pitting reasons for the formation, carried out dfferent materials polyethylene gas pipe butt welding weld pitting test tubes of different materials, water absorption and moisture content of materials of different quality weld pipe butt welding degree of influence, and carried out by thermal drying method to reduce polyethylene butt weld pitting pilot study to find a simple and effective in reducing weld pitting application method.
Keywords:Polyethylene gas pipe 1前言
Pmg
热熔对接焊在20世纪60年代就成功应用于聚乙烯燃气管道的连接，是聚乙烯燃气管道施工中主要的连接方法之一。随着聚乙烯燃气管道在国内燃气输配系统中应用得越来越普遍，存放环境太潮或存放时间过久的聚乙烯燃气管材进行热熔焊接，在焊口处产生麻点的现象在施工中经常出现，过大过密的气孔会导致焊接接头安全性能不足甚至失效，如何减少麻点提
万方数据
Pitting
Heat drying
method
高焊接接头的安全性成为各施工单位垂待解决的突出问题。
2对接焊焊口麻点形成原因
聚乙烯燃气管材是使用燃气专用聚乙烯混配料挤出加工成型制造而来。所谓燃气专用聚乙烯混配料是指在聚乙烯中加人必要的、均匀分散的助剂后得到的专用混配料。这些加入到聚乙烯中均匀分散的助剂主
2014/03总第469期125