铝含量对Q345E温角钢低温性能的影响
孙贵平
（河钢集团宜钢公司一钢轧厂，河北宣化075100）
Total No. 259 2017,Number7
摘要：在《GB/T1591-2008低合金高强度结构钢》标准中Q345E钢材的化学成分基础上，根据模拟计算和大量文献，设计了Q345E钢的微合金成分，并试生产了不同铝含量的Q345E角钢。研究了铝含量对 Q345E耐低温角钢钢材性能的影响。研究结果表明：高铝含量对增加Q345E角钢低温韧性有较大作
用，且钢中铝含量在0.020%~0.030%范围内低温韧性最好。关键词：铝含量：Q345E耐低温角钢；低温性能；影响
中图分类号：TG142.1
文献标识码：A
doi : 10. 13630/j. cnki. 13 1172. 2017. 0708
文章编号：10065008（2017)07003304
EFFECTOFALUMINUMCONTENTONLOW
TEMPERATUREPERFORMANCEOFO345EANGLESTEEL
Sun Guiping
(No. 1 Rolling Mill, HBIS Group Xuansteel Company , Xuanhua, Hebei, 075100)
aee structural steel" standard, the micro alloy composition of Q345E steel was designed with simulatior calculation and a flood of literature, and the trial production of Q345E steel with different aluminum content was made. The effect of aluminum content on the properties of Q345E low temperature angle steel was studied. The result shows that the high aluminum content has a great effect on improving the low temperature toughness of Q345E angle steel, and the low temperature toughness is the best with the aluminum content range as 0.020%~0.030%
Key Words : aluminum content; Q345E low temperature angle steel; low temperature performance; influence
引言
按照我国电网规划，将在东北、华北、西北地区
建设多条输电线路，这些地区冬季气温较低，最低温度将达-40℃以下，输电铁塔用材规格大、载荷大、施工条件恶劣。自前我国国网智能电网研究院已对高寒地区输电铁塔用钢的开发进行了大量的研究工作，并已具备相应的技术及理论基础，如何将其应用于高寒地区输电的铁塔建设引起了广泛关注。我国钢结构设计规范、输电线路铁塔设计规范均是通过控制钢材的冲击韧性指标对钢结构的低温断裂行为进行控制的。而长期以来，Q345级角钢产品普遍存在低温条件下韧性偏低、波动较大、难以满足客
收稿日期；2017-04-02
作者简介：孙贵平（1970－），男，高级工程师，2011年毕业于河北联合大学冶金工程专业，现在河钢集团宣钢公司一钢轧厂从事炼钢生产，工艺管理工作,Email;1720816569@qq.com
万方数据
户使用要求的问题。因此，生产具有良好耐低温性能的Q345E级角钢具有重大现实意义。宜宣钢从合金成分设计的角度出发，力求在尽量不调整轧制工艺的前提下，通过添加合金元素、优化各成分配比，生产出Q345E耐低温角钢。
本文主要在已有Q345E合金成分设计和实验室实验的基础上，进行现场工业试生产，试制不同铝元素含量的Q345E角钢。对工业试制样品进行系统分析，研究铝含量变化对材料组织性能的影响，探讨提高其低温韧性的微观机理，为在后续批量生产过程中不断优化工艺制度，提供理论依据。
Q345E耐低温角钢成分设计
1
国家标准对耐候钢成分、性能的规定
1.1
化学成分对钢的性能有很大的影响，因而相关标准对角钢的化学成分均有严格要求。钢的性能直接作用于使用过程，因此国家标准对耐候钢的化学
33