焙烧工艺对球团矿还原性能
的影响
李英魁
（河钢集团承钢公司炼铁厂，河北承德067002）
Total No. 253 2017,Numberl
摘要：针对承钢球团矿的原料特点，研究了不同膨润土配比和焙烧工艺条件对承钢钒钛磁铁矿球团还原性能的影响。试验结果表明，承钢竖炉球团造球过程中，膨润土配比控制在2%~3%之间，焙烧温度控
制在1200~1250℃，焙烧时间控制在30min，对球团矿的中温还原性有利。关键词调：钛磁铁矿球团；影润土配比；焙烧温度；焙烧时间；还原性能
中图分类号：TF046.2
文献标识码：A
doi;10. 13630/j. cnki. 13 1172. 2017. 0103
文章编号：10065008(2017)010011-04
INFLUENCEOFROASTINGPROCESS CONDITIONONPELLETREDUICBILITY
Li Yingkui
(Ironworks, Hesteel Group Chengsteel Company, Chengde, Hebei, 067002)
Abstract: Based on the characteristic of raw materials for pellet in Cheng Steel, the influence of different bentonite proportion rate and roasting process condition on the reducibility of vanadium titano magnetite pellet is researched. It is showed from the test that the following conditions are favor to medium temperature reducibility of pellet: in balling process with shaft furnace, bentonite controlled within 2% to 3% , roasting temperature within 1 200 to 1 250 °C , roasting time as 30 minutes.
Key Words: vanadium titano - magnetite pellet; bentonite proportion rate; roasting temperature; roasting time: reducibility
引言
钢铁企业通常把球团矿的品位和抗压强度作为
衡量其质量的重要指标，但随着球团矿使用比例的增加，球团矿的综合性能对高炉冶炼的影响越来越重要。不仅球团矿品位、抗压强度等冷态指标很重要，而且高温冶金性能也非常重要。而承钢球团矿的主要原料为钒钛磁铁矿，由于钒钛磁铁矿的特殊性质，导致承钢球团矿的含铁品位比较低，球团矿中铁矿物的数量比较少，而液相粘结相的还原性能又比较差，给高炉冶炼过程带来不利影响。为此，承钢对膨润土配比和焙烧工艺条件对球团矿还原性能的影响进行了研究，提出了承钢钒钛磁铁矿球团合理的收稿日期：20161025
作者筒介：李英魁（1972-），男，高级工程师，工程硕士，1996年毕业于华北理工大学钢铁冶金专业，现在河钢集团承钢公司从事高护冶
炼工作，Email:13831472275@163.com 万方数据
造球、焙烧参数，以期改善球团矿的冶金性能。
试验原料的理化性能
试验所用铁精矿粉和膨润土取自于承钢生产现场，其物理化学性能如表1所示。
铁精矿粉和膨润
土的化学成分、粒度组成如表2、表3所示。
表1
Tab.1 品种
膨润土的物理化学性能
Physical and chemical properties of bentonite
胶质价/
(mL/15 g)
建平膨润士
294
膨胀容/(mL/g) 62
吸蓝量/(g/100 g) 36
相对蒙脱石含量/% 81.45
11