总第260期 2017年第8期
河北冶金 HEBEI METALLURGY
提高精轧机组刚度实践
潘腾刘伟赵松
（河钢集团邯钢公司2250热轧厂，河北邯郸056003）
Total No. 260 2017,Number8
摘要：为了解决2250热轧生产线精轧机组刚度下降、轧制稳定性较差的问题，在对精轧机组刚度下降原因进行分析的基础上，提出了恢复提升精轧机组刚度的相应措施。通过间隙测量和轴承座加垫等方法修正轧机两侧垂直方向和交叉方向的物理偏差，精轧机刚度得到明显提升，为品种钢的批量稳定轧制提供了根本保障，
关键词：精轧机：刚度；实践
中图分类号：TG333.13
文献标识码：B
doi:10. 13630/j. cnki. 13 1172. 2017. 0812
文章编号：10065008（2017)08004203
PRACTICEOFIMPROVING
THESTIFFNESSOFFINISHINGMILL
Pan Teng, Liu Wei, Zhao Song
(2250 Hot Rolling Mill, HBIS Group Hansteel Company ,Handan, Hebei, 056003 )
Abstract : Based on the reason analysis of stiffness degradation, the measures of stiffness recovery of finishing mill were put forward in order to solve the problem of poor stiffness and poor rolling stability of finishing mil on 2250 Hot Rolling Line. By measuring clearance and adding bearing seat cushion, the physical deviation in vertical direction and cross direction of both sides of rolling mill is corrected, and the rolling mill stiffness has
improved significantly, which provides the fundamental guarantee for stable rolling of quality steel Key Words : finishing mill;stiffness; practice
0
引言
刚度是反映轧机结构性能的重要参数，也是轧
机所能获得轧制精度的主要指标。轧机刚度为编制新的合理轧制规程提供必要的设备性能数据，并且为实现带钢厚度的自动调节及计算机控制提供数据。邮宝2250热轧生产线自2008年8月份投产以来，由于设备维护没有持续跟进，部分设备老化，精轧机组7架轧机刚度均有不同程度下降；交工时的刚度测试结果显示，精轧机刚度为7700kN/mm。如果按照7000kN/mm合计刚度计算，2014年7月测量结果显示，刚度保持率仅为73.96%。刚度的变化对轧制稳定性影响很大，容易导致用尾、废钢的增加。随着该生产线品种钢、薄规格比例逐年增加，设备精度要求已经不能满定稳定生产高质量产品的
收稿日期；2017-04-12
作者简介：潘腾（1986－），男，助理工程师，2008年毕业于重庆大学材料科学与工程专业，现在河钢集团邯钢公司2250热轧厂工作，E mail:403974355@ qq. com
42
万方数据
要求。为了解决2250热轧生产线精轧机组刚度下降、轧制稳定性较差的问题，在对精轧机组刚度下降原因进行分析的基础上，提出了恢复提升精轧机组刚度的相应措施策略。通过间隙测量和轴承座加垫等方法，精轧机刚度得到明显提升，为品种钢批量稳定轧制提供了根本保障。
1
刚度下降对轧制稳定性的影响
(1)轧制生产中，坏料厚度波动及其力学性能
不均句等容易起板厚偏差，要求转机具有较大的刚度。轧机的刚度愈大，则出口板的厚偏差愈小。
(2）当轧机的刚度变化时，精轧机的设定模型就会出现偏差，导致轧机控制误差增大。例如，F3 的刚度下降10.8%，可能会造成F3机架的辊缝设定误差达到10%。
（3）当轧机两侧刚度产生不对称变化时，轧机在不同的轧制压力条件下就会出现不对称弹性变形，从而造成辑辊缝楔形。由此带来的楔形变化不会显示操作台上，给操作人员控制板形带来了很多困