总第262期 2017年第10期
河北冶金 HEBEI METALLURGY
冷轧支承辊辊颈的堆焊修复
杜瑞岭，张杨
（河钢集团唐钢公司，河北唐山063016）
Total No. 262 2017,Number10
摘要：以铸铁冷轧支承辊为例，采用堆焊修复方法对支承辊磨损的轴承位进行了尺寸恢复与强化 Φ3.2mmZ308焊条采用辊颈表面预处理→辊颈局部预热→堆焊→缓冷的堆焊工艺，克服了铸铁焊接难度大、易产生焊接裂纹的问题，成功地对支承辊实施了局部修复。堆焊修复后的支承辊过钢量接近
40万t，仍然能够正常使用，创造了可观的经济效益。关键词：冷轧支承辑；辊颈；堆焊；修复
中图分类号：TG333.8
文献标识码：B
doi:10.13630/j. cnki.13 1172.2017.1012
文章编号：10065008（2017)10=0056=02
SURFACINGWELDINGREPAIRO COLDROLLEDSUPPORTROLLNECK
DuRuiling,ZhangYang
(HBIS Group Tangsteel Company, Tangshan, Hebei, 063016)
Abstract: Taking the cold rolled support roll of cast iron as an example, the worn bearing seat is restored and strengthened by surfacing welding repair. With @ 3. 2 mm Z308 welding rod, the process is adopted of sur-face pretreatment of roll neck, local preheating of roll neck, surfacing welding repair and slow cooling, which overcomes the welding difficulties and welding crack of cast iron. The partial repair of the support roll er has been successfully carried out. After the surfacing repair, the support roller's load has been close to
400,o00 t, which still can use normally and the considerable economic efficiency got Key Words: cold rolled support roll; roll neck; surfacing welding; repair
引言
0
支承辑是冷轧板带生产线的重要备件之一，其质量的优劣直接关系到板带的质量。近年来，各大钢厂普遍采用堆焊方式对达到极限尺寸的支承辊进行尺寸恢复与强化，在降低修复成本的同时，能够提高轧辑的使用寿命和产品质量。目前，冷轧板带轧机用支承辑儿乎均为合金锻钢辑，成分以Cr3、Cr5 锻钢为主。而对支承辑堆焊的研究绝大多数也以 Cr3、Cr5材质的锻钢轧辊堆焊修复为主，对于复合铸铁铸造冷轧支撑辑的堆焊修复的研究鲜有报道。
某厂冷轧板厂从国外进口1批冷轧支承辑，整体支承辊采用无线冷硬球磨铸铁铸造，辊身直径 1000mm，辊颈580mm，总长3550mm，重15t,每
收稿日期：2017-07-05
作者简介：杜瑞岭（1964－），男，高级工程师，硕士，2003年毕业于河北工业大学技术经济与管理专业，现在河钢集团唐钢公司从事技术研发工作,Email:ddv1059@163.con
56
万方数据
只支承辊价值200万元左右。由于支承辑的图纸设计间题，导致辑颈轴承位处的尺寸比实际要求尺寸小0.3mm，从而使辑颈不能与轴承正常配合。如果不做处理，则该支承辊只能报废，这样将造成近千万元的直接经济损失。为避免这一较大的经济损失，在充分分析球磨铸铁焊接性的基础上，合理地选择堆焊工艺路线和堆焊材料，克服了铸铁焊接性差、易产生焊接裂纹的难题，成功地对这批支承辊轴承位进行了堆焊恢复。
1
堆焊材料
冷硬铸铁支承辊的含碳量高、杂质多、可焊性极
差，由于熔池凝固快，焊缝及近缝区极易产生白口及脆性马氏体组织。同时，支承辊又是十几吨重的庞然大物，刚性大、塑性差，焊接的局部不均匀加热、快速冷却，容易产生较大的焊接应力，导致焊缝和热影响区产生裂纹。为克服铸铁焊接性差的难题，合理的选择堆焊材料是保证堆焊成功的关键。本文中实