南方金属 SOUTHERN METALS
高碳钢线材控氮工艺研究
胡心光1,2，李亚厚"2，张俊粉1,2
Sum.208 February2016
（1.河北省钒钛工程技术研究中心，河北承德067102；2.河北钢铁集团承钢公司，河北承德067102）
摘要：针对高碳钢线材77MnCrV氮含量超标间题，调查分析了炼钢各工序的增氮关键控制点，提出相应的改进措
施，降低了钢中氮含量，连铸坏质量得到明显改善，关键词：炼钢；控氮；保护
中图分类号：TF703
文献标识码：A
StudyonProcessof ControllingNitrogenContentinHighCarbon Steel Wires
HU Xin-guang'*, LI Ya-hou'-2, ZHANG Jun-fen'-2
(1. Engineering and Technology Research Center of Vanadium and Titanium, Chengde, Hebei, 067102, P. R. China;
2. Chengde Branch, Hebei Iron & Steel Co. , Lid. , Chengde, 067102, P. R. China)
Abstract: Study on the problem of excessive nitrogen content in high carbon steel wire rods was carried out, the effect of nitrogen content on the drawing performance of high carbon steel wire rods was analyzed, and the key process control points of the 77MnCrV steel-making process were investigated. The corresponding improvement measures were put forward, and
the quality of continuous casting billets were improved obviously Key words: steel-making; nitrogen content control; protection
0引言
相关资料表明1，氮会使钢产生时效、蓝脆等质量问题.当钢中氮含量较高时，易形成气泡和组织疏松，还会降低钢的延伸率、断面收缩率等.而作为钢的拉拔性能重要指标的钢的延伸率和断面收缩率与钢中氮含量存在着明显的联系，钢的拉拔性能随钢中氮含量下降而有所改善.因此，如何控制线材品种的氮含量超标问题，是生产过程中的关键环节.河北钢铁集团承钢公司（以下简称“承钢”）长材事业二部在生产高碳线材77MnCrV过程中，对铸坏气体 N含量进行检验，平均为75×10-6.最高为96× 10-°.严重影响了线材的拉拔性能.针对此问题，通过对炼钢各工序增氮原因进行分析，采取了有效的
控制措施，氮含量超标问题得到有效控制收稿日期：2015-08-28
1氮含量对高碳钢线材拉拨性能的影响
氮在钢中属于微量元素，含量较低，但对钢质却有很大的影响[2]，相关研究表明，氮在α-Fe中的溶解度随温度的降低变化很大，590℃时可达 0.1%.但在室温时则降到0.001%以下，当钢自高温快速冷却时，多余的氮来不及析出，α一Fe成为含氮过饱和固溶体，但这种过饱和固溶体是不稳定的，随着时间的延续，氮将以FeN。形式弥散析出，使钢的强度、硬度提高，塑性、韧性降低.这种性能随时间的延续而发生变化的效应称为“时效”.钢中的含氮量越高，时效倾向越严重.一般认为，只有当氮含量低于60×10-时，才能减轻时效硬化3}.氮和氢的综合作用会使钢坏产生结疤和皮下气泡，因而在乳制过程中产生裂纹，致使在钢丝的拉拨过程中发生势裂和断裂.总之，氮会使钢产生时效、蓝脆等质量问题，当钢中氮含量较高时，易形成气泡和组织疏松，
作者简介：胡心光（1982-），男，2010年东北大学冶金物理化学专业硕士研究生毕业，工程师